Effects of defects on the tensile strength of rigid polyurethane foamed plastics
-
摘要: 针对几种密度的无缺陷和含缺陷的硬质聚氨酯泡沫塑料试件进行了拉伸实验,研究了材料的强度性质,并且探讨了各种缺陷形式对拉伸强度的影响.实验结果表明,材料经长期放置后(约6年)其拉伸强度并未发生明显的变化,且与相对密度的二次幂成正比;此外,发现缺陷形式对聚氨酯泡沫塑料的拉伸强度有明显的影响,且弧形缺陷对材料拉伸强度的影响具有明显的尺寸效应.Abstract: The tensile tests have been done for different densities polyurethane rigid foam (PURF) specimens with and without defects. On the basis of experiments, the strength of PURF is investigated and the effects of defect with different kind and different size on the ultimate strength of PURF are discussed at the same time. The result of experiments shows that the tensile strengths of PURF specimens stored in a long time (about 6 years) have not been changed and they are proportional to the square of relative densities of PURF. It also found that the form of defects has significant effects on the tensile strength of PURF and if the defects of specimens have the shape of an arc, they have significant size effect of defects on their tensile strengths.
-
Key words:
- foamed plastics /
- mechanical properties /
- defects /
- tensile test
-
[1] 卢子兴,寇长河,李怀祥. 泡沫塑料拉伸力学性能的研究[J]. 北京航空航天大学学报,1998,24(6):646~649 Lu Zixing, Kou Changhe, Li Huaixiang. Investigation into tensile mechanical properties of PUR foam plastics [J]. Journal of Beijing University of Aeronautics and Astronautics, 1998,24(6):646~649 (in Chinese) [2] 卢子兴,朱汪鲲,寇长河,等. 聚氨酯泡沫塑料的强度与断裂韧性[J]. 力学学报,2000,32(5):627~631 Lu Zixing, Zhu Wangkun, Kou Changhe, et al. Investigation on the fracture properties of polyurethane rigid foam plastics [J]. Acta Mechanica Sinica, 2000, 32(5):627~631(in Chinese) [3] 卢子兴,赵明洁. 泡沫塑料力学性能研究进展[J]. 力学与实践,1998,20(2):1~9 Lu Zixing, Zhao Mingjie. Development of investigation into mechanical properties of foamed plastics [J]. Mechanics and Engineering, 1998,20(2):1~9(in Chinese) [4] Andrews E W, Gibson L J. The Influence of cracks, notches and holes on the tensile strength of cellular solids [J]. Acta Mater, 2001,49:2975~2979 [5] Andrews E W, Gibson L J. The influence of crack-like defects on the tensile strength of an open-cell Aluminum foam[J]. Scritpta Mater, 2001,44:1005~1010 [6] Chen C, Fleck N A, Lu T J. The mode I crack growth resistance of metallic foams[J]. J Mech Phy Solids, 2001,49:231~259 -
点击查看大图
计量
- 文章访问数: 2806
- HTML全文浏览量: 56
- PDF下载量: 915
- 被引次数: 0
下载: