Comparison between quasi-static indentation testing and drop-weight impact testing on delamination onset damage
-
摘要: 为了研究复合材料层合板的分层起始载荷,对不同材料体系和不同铺层数的复合材料层合板进行了准静态压痕试验和落锤冲击试验.得到了复合材料层板的分层起始载荷和冲击分层损伤能量门槛值,并对损伤情况进行了分析.结果表明,层合板的落锤冲击试验的分层起始载荷与冲击能级有关,并且分层起始载荷值随冲击能级提高而增加;准静态压痕试验的分层起始载荷值要低于低速冲击试验的分层起始载荷值;当冲击能量达到层板分层损伤能量门槛值时,层板发生大量分层损伤,层合板刚度出现急剧下降.Abstract: To discuss the delamination onset load, quasi-static indentation tests and drop-weight impact tests were performed. The effects of the material and plying pattern on the delamination onset load were also studied. Moreover, the delamination threshold energy levels were found and the corresponding damage was analyzed. The results show that the delamination onset load increases along with the impact energy, and the delamination onset load in the quasi-static indentation is lower than in the low-velocity impact. Massive delamination happens in laminate panels when the energy reaches the delamination threshold energy, and the rigidity descends rapidly.
-
Key words:
- quasi-static indentation /
- low-velocity impact /
- delamination onset load
-
[1] 杨乃宾,张怡宁.复合材料结构设计[M]. 北京:北京航空航天大学出版社, 2003:321-330 Yang Naibin, Zhang Yining. Composite structure design[M]. Beijing: Beijing University of Aeronautics and Astronautics Press, 2003:321-330(in Chinese) [2] Nettles A T, Douglas M J. A comparison of quasi-static indentation to low-velocity impact . NASA/TP-2000-2210481, 2000 [3] Swanson S R. Limits of quasi-static solutions in impact of composite structures[J]. Composites Engineering, 1992,2(4):261-267 [4] Kwon Y S, Sankar B V. Indentation-flexure and low-velocity impact damage in graphite epoxy laminates[J]. Journal of Composites Technology and Research, 1993,15(2):101-111 [5] Kaczmarek H, Maison S. Comparative ultrasonic analysis of damage in CFRP under static indentation and low-velocity impact[J]. Composites Science and Technology, 1994,51(1):11-26 [6] Lee S M, Zahuta E. Instrumented impact and static indentation of composites[J]. Journal of Composite Materials, 1991,25(2):204-222 [7] ASTM D 7136—05, Test method for measuring the damage resistance of a fiber-reinforced polymer-matrix composite to a drop-weight impact event[S] [8] ASTM D 6264—98(04), Test method for measuring the damage resistance of a fiber-reinforced polymer-matrix composite to a concentrated quasi-static indentation force[S] [9] 关志东,赵伟. FC落锤式冲击试验机的研制及T300／QY8911层合板低速冲击损伤的试验研究[J].复合材料学报, 2005,22(增刊):27-31 Guan Zhidong, Zhao Wei. FC impact testing machine and the research of low velocity impact damage of T300/QY8911 composite plates[J]. Acta Materiae Compositae Sinica, 2005, 22(Supplement):27-31(in Chinese) [10] Davies G A O, Zhang X, Zhou G, et al. Numerical modeling of impact damage[J]. Composites, 1994,25(5):342-350 -
点击查看大图
计量
- 文章访问数: 3446
- HTML全文浏览量: 14
- PDF下载量: 1416
- 被引次数: 0
下载: