Niyama判据对铸件缩孔缩松预测的适用性

潘利文 郑立静 张虎 高文理

潘利文, 郑立静, 张虎, 等 . Niyama判据对铸件缩孔缩松预测的适用性[J]. 北京航空航天大学学报, 2011, 37(12): 1534-1540.
引用本文: 潘利文, 郑立静, 张虎, 等 . Niyama判据对铸件缩孔缩松预测的适用性[J]. 北京航空航天大学学报, 2011, 37(12): 1534-1540.
Pan Liwen, Zheng Lijing, Zhang Hu, et al. Applicability of shrinkage porosity prediction for casting with Niyama criterion[J]. Journal of Beijing University of Aeronautics and Astronautics, 2011, 37(12): 1534-1540. (in Chinese)
Citation: Pan Liwen, Zheng Lijing, Zhang Hu, et al. Applicability of shrinkage porosity prediction for casting with Niyama criterion[J]. Journal of Beijing University of Aeronautics and Astronautics, 2011, 37(12): 1534-1540. (in Chinese)

Niyama判据对铸件缩孔缩松预测的适用性

详细信息
    作者简介:

    潘利文(1978-),男,广西武鸣人,博士生,plw11@sina.com.

  • 中图分类号: TG 245

Applicability of shrinkage porosity prediction for casting with Niyama criterion

  • 摘要: 应用ProCAST有限元模拟软件包的Niyama判据对TiAl合金十字板状铸件中肉眼可见的宏观缩孔缩松进行了预测,并通过实验进行了验证.结果表明:对于Ti-47Al-2Cr-2Nb合金十字板状铸件,判据值主要受到铸件壁厚(冷速)的影响,判据值随铸件壁厚的增加而增大,宏观缩孔缩松最严重的区域不是判据值最小的区域,而判据值最小的区域只有显微缩松而没有宏观缩孔缩松,所以无法根据判据值大小来确定宏观缩孔和宏观缩松产生的位置及大小.分析表明,Niyama判据是一种基于枝晶间显微缩松的预测判据,其判据值适用于评定显微缩松产生的倾向性,可以较准确地预测出显微缩松产生的位置.由于宏观缩孔和宏观缩松形成机理与显微缩松不同,所以不宜用于壁厚悬殊的复杂铸件宏观缩孔缩松的预测.

     

  • [1] Niyama E,Uchida T,Morikawa M,et al.A method of shrinkage prediction and its application to steel casting practice[J].AFS Int Cast Met J,1982,52(9):52-63 [2] Lee P D,Chirazi A,See D.Modeling microporosity in aluminum-silicon alloys:a review[J].Journal of Light Metals,2001,1(1):15-30 [3] 熊守美,许庆彦,康进武.铸造过程模拟仿真技术[M].北京:机械工业出版社,2004:181-182 Xiong Shoumei,Xu Qingyan,Kang Jinwu.Analog simulation technique for casting process[M].Beijing:China Machine Press,2004:181-182(in Chinese) [4] 李嘉荣,柳百成.G/R 法在球铁件缩孔缩松预测中的应用研究[J].铸造,1998(7):9-13 Li Jiarong,Liu Baicheng.Application of G/R method to prediction of shrinkage cavity and porosity in ductile iron casting[J].Foundry,1998(7):9-13(in Chinese) [5] 李殿中,苏仕方,王君卿,等.缩孔缩松判据函数及其在IN738合金板类铸件中的应用[J].铸造,1998(6):13-17 Li Dianzhong,Su Shifang,Wang Junqing,et al.The shrinkage porosity functions and its application in IN738 castings[J].Foundry,1998(6):13-17(in Chinese) [6] 崔吉顺,李文珍.铸件缩孔缩松多种预测判据的应用[J].清华大学学报:自然科学版,2001,41(8):5-8 Cui Jishun,Li Wenzhen.Criteria for prediction of shrinkage cavities and porosity in castings[J].Journal of Tsinghua University:Science and Technology,2001,41(8):5-8(in Chinese) [7] 王春乐.铸钢件缩孔缩松预测方法及判据浅析[J].山西机械,2003(4):8-10 Wang Chunle.Analysis on prediction methods and criteria of shrinkage cavity and porosity in steel castings[J].Shanxi Machine,2003(4):8-10(in Chinese) [8] 贾宝仟,柳百成.铸件缩松缩孔判据G/T的理论基础及应用[J].铸造,1996(4):13-15 Jia Baoqian,Liu Baicheng.Theoretical derivation of criterion G/T for prediction the shrinkage cavity and porosity in castings and its application[J].Foundry,1996(4):13-15(in Chinese) [9] Fu P X,Kang X H,Ma Y C,et al.Centrifugal casting of TiAl exhaust valves[J].Intermetallics,2008,16(2):130-138 [10] Tavakoli R,Davami P.Automatic optimal feeder design in steel casting process[J].Comput Methods Appl Mech Engrg,2008,197(9-12):921-932 [11] Zhu J D,Cockcroft S L,Maijer D M.Modeling of microporosity formation in A356 aluminum alloy casting[J].Metallurgical and Materials Transaction A,2006,37A:1075-1085 [12] 李文,张建民,关振中.Ti-Al相图的高温液相线[J].应用科学学报,1996,14(4):391-397 Li Wen,Zhang Jianmin,Guan Zhenzhong.Liquidus curves of the high-temperature phase fields in the Ti-Al system [J].Journal of Applied Sciences,1996,14(4):391-397(in Chinese) [13] Sung Siyong,Kim Yongjia.Modeling of titanium aluminides turbo-charger casting[J].Intermetallics,2007(15):468-474 [14] 卜昆,李永毅,董一巍,等.单晶叶片铸造过程中界面换热系数的确定[J].铸造,2009,58(3):225-228 Bu Kun,Li Yongyi,Dong Yiwei,et al.Determination of interfacial heat transfer coefficient during single crystal blade casting process[J].Foundry,2009,58(3):225-228(in Chinese) [15] Guo Zhipeng,Xiong Shoumei.Relationship between metal-die interfacial heat transfer coefficient and casting solidification rate in high pressure die casting process[J].Acta Metallurgica Sinica,2009(1):102-106 [16] 贾宝仟,柳百成.基于枝晶间渗流理论的砂型铸件缩孔缩松判据G/T的讨论及应用[J].热加工工艺,1996(2):34-36 Jia Baoqian,Liu Baicheng.Theoretical derivation and discussion of criterion G/Tbased on fluid penetration theory for shrinkage cavity and porosity prediction of casting[J].Hot Working Technology,1996(2):34-36(in Chinese) [17] 陈国桢,肖柯则,姜不居.铸件缺陷和对策手册[M].北京:机械工业出版社,2003:157-158 Chen Guozhen,Xiao Keze,Jiang Buju.Casting flaw and countermeasure manual[M].Beijing:China Machine Press,2003:157-158(in Chinese)
  • 加载中
计量
  • 文章访问数:  3804
  • HTML全文浏览量:  248
  • PDF下载量:  1385
  • 被引次数: 0
出版历程
  • 收稿日期:  2010-09-15
  • 网络出版日期:  2012-12-30

目录

    /

    返回文章
    返回
    常见问答