复合材料加筋板筋条修理后的压缩性能

赵闯 聂恒昌 郭霞 关志东

赵闯, 聂恒昌, 郭霞, 等 . 复合材料加筋板筋条修理后的压缩性能[J]. 北京航空航天大学学报, 2014, 40(6): 834-838. doi: 10.13700/j.bh.1001-5965.2013.0431
引用本文: 赵闯, 聂恒昌, 郭霞, 等 . 复合材料加筋板筋条修理后的压缩性能[J]. 北京航空航天大学学报, 2014, 40(6): 834-838. doi: 10.13700/j.bh.1001-5965.2013.0431
Zhao Chuang, Nie Hengchang, Guo Xia, et al. Compression performance of composite stiffened panel after stiffener repair[J]. Journal of Beijing University of Aeronautics and Astronautics, 2014, 40(6): 834-838. doi: 10.13700/j.bh.1001-5965.2013.0431(in Chinese)
Citation: Zhao Chuang, Nie Hengchang, Guo Xia, et al. Compression performance of composite stiffened panel after stiffener repair[J]. Journal of Beijing University of Aeronautics and Astronautics, 2014, 40(6): 834-838. doi: 10.13700/j.bh.1001-5965.2013.0431(in Chinese)

复合材料加筋板筋条修理后的压缩性能

doi: 10.13700/j.bh.1001-5965.2013.0431
详细信息
    作者简介:

    赵 闯(1989- ),男,天津人,硕士生,zcmacaron@sina.cn.

  • 中图分类号: V214.8

Compression performance of composite stiffened panel after stiffener repair

  • 摘要: 承受压缩载荷时,筋条损伤往往造成复合材料加筋板结构的严重失效.针对筋条壁板脱黏、腹板分层、上缘条损伤3种情况分别设计了相应的修理方案并制作了试验件.为保证压缩载荷的均匀施加,设计制作了加筋板试验专用夹具,含有固定试验件的卡槽和保证加载方向沿竖直方向的导轨.筋条修理后的复合材料加筋板的轴向压缩试验表明不同修理部位、不同修理方法对加筋板的力学性能影响不同.有限元分析表明加筋板的屈曲模态、整体破坏模式以及板-筋胶层的破坏情况都受到修理方案的影响.

     

  • [1] Hart-Smith L J. Adhesive bonded double lap joints[R].NASA CR-112235,1973
    [2] Hart-Smith L J. Adhesive bonded single lap joints[R].NASA CR-112236,1973
    [3] Hart-Smith L J. Adhesive bonded scarf and stepped-lap joint[R].NASACR-112237,1973
    [4] Hassan N K, Mohamedien M A,Rizkalla S H.Finite element a- nalysis of bolted connections for PFRP composites[J].Composites Part B:Engineering,1996,27(3/4):339-349
    [5] Kassapoglou C. Stress determination at skin-stiffener interfaces of composite stiffened panels under generalized loading[J].Journal of Reinforced Plastics and Composites,1994,13(6):555-571
    [6] Zhang H, Motipalli J,Lam Y C,et al.Experimental and finite element analyses on the post-buckling behaviour of repaired composite panels[J].Composites Part A:Applied Science and Manufacturing,1998,29(11):1463-1471
    [7] Mahdi S, Kinloch A J,Crisfield M A,et al.The mechanical performance of repaired stiffened panels.part II:finite element modelling[J].Composites Part B:Engineering,2002,33(5):355-366
    [8] 李航,矫桂琼, 赵龙,等.含切口复合材料加筋板的压缩剩余强度研究[J].工程力学,2011,176(8):133-137 Li Hang,Jiao Guiqiong,Zhao Long,et al.Progressive failure analysis of stiffened composite plate with notch[J].Engineering Mechanics,2011,176(8):133-137(in Chinese)
    [9] 孙立,许希武, 徐焜.含脱粘损伤的复合材料加筋板压缩破坏渐进损伤数值分析[J].材料科学与工程学报,2009,27(5):740-744 Sun Li,Xu Xiwu,Xu Kun.Progressive damage analysis of stiffened composite panels with debonding damage under compressive load[J].Journal of Materials Science and Engineering,2009,27(5):740-744(in Chinese)
    [10] 刘从玉,许希武, 陈康.考虑脱粘的复合材料加筋板屈曲后屈曲及承载能力数值分析[J].复合材料学报,2010, 27(6): 158-166 Liu Congyu,Xu Xiwu,Chen Kang.Buckling,post-buckling and collapse analysis of stiffened composite panels with debonding damage[J].Acta Materiae Compositae Sinica,2010,27(6):158-166(in Chinese)
    [11] 常园园,许希武, 郭树祥.压缩载荷下复合材料整体加筋板渐进损伤非线性数值分析[J].复合材料学报,2011, 28(4): 202-211 Chang Yuanyuan,Xu Xiwu,Guo Shuxiang.Nonlinear progressive damage analysis of integral stif fened composite panels under compressive load[J].Acta Materiae Compositae Sinica,2011,28(4):202-211(in Chinese)
  • 加载中
计量
  • 文章访问数:  1237
  • HTML全文浏览量:  22
  • PDF下载量:  473
  • 被引次数: 0
出版历程
  • 收稿日期:  2013-07-29
  • 网络出版日期:  2014-06-20

目录

    /

    返回文章
    返回
    常见问答