Selection of Catalysts Used in the Preparation of WaterSoluble Phenolic Resol Resin

Yang Guang

Dept. of Material Science and Engineering, Beijing University of Aeronautics and Astronautics

摘要

摘要: 通过理论分析和实验总结,研究了不同种类的碱性催化剂对酚醛树脂水溶性的影响,最后确定同时使用某种叔胺类化合物和少量氢氧化钡作为合成水溶性酚醛树脂的催化剂.在适宜的反应条件下,制得了游离酚含量和游离甲醛含量均较小的水溶性酚醛树脂.这种水溶性酚醛树脂可用于电气绝缘等诸方面.
- 酚醛树脂 /
- 水溶性 /
- 催化剂 /
- 制备 /
- 氢氧化钡 /
- 叔胺
Abstract: The effect of the kinds of basic catalysts on the preparation of water-soluble phenolic resol resin was investigated. The water-soluble resol was prepared by the reaction between phenol and formaldehyde with molar ratio 1:1.2~1.5 in the presence of catalysts at 80~85℃. The catalysts were made up of a kind of tertiary amine and a small amount of barium hydroxide. Free phenol content a nd free formaldehyde content in the water-soluble resol were not more than 10% and 1.4% respectively. This water-soluble resol is widely used in many applica tions such as plywood and insulation laminate.
- phenolic aldehyde resins /
- water solubility /
- catalyst /
- preparation /
- barium hydro xide /
- tertiary amine

HTML全文

参考文献(1)

[1] 唐传林,季承钧,单书发. 绝缘材料工艺原理[M]. 北京∶机械工业出版社,1993 Tang Chuanlin,Ji Chengjun,Shan Shufa. Principle of insulation materials pr ocess[M]. Beijing:China Machine Press,1993(in Chinese) [2] 叶家镛,费敏明,张显友. 改性水溶性酚醛树脂及其应用[J]. 哈尔滨电工学院学报,1987,10(4)∶383~389 Ye Jiayong,Fei Minming,Zhang Xianyou. Modified water soluble phenolic resin an d its application[J]. HIET Journal,1987,10(4):383~389(in Chinese) [3] 黎钢,徐进,毛国梁等. 水溶性酚醛树脂作为水基聚合物凝胶交联剂的研究[J]. 油田化工,2000,17(4):310~313 Li Gang,Xu Jin,Mao Guoliang, et al. Water-soluble phenol-formaldehyde re sin as crosslinker for aqueous polymer gelling fluids used in depth reservoir pe rmeability control[J]. Oilfield Chemistry,2000,17(4):310~313(in Chinese) [4] Astarloa-Aierbe G,Echeverria J M,Vazquez A,et al. Influe n ce of the amount of catalyst and initial pH on the phenolic resol resin formatio n[J]. Polymer,2000,41(9):3311~3315 [5] Manfredi L B,de la Osa O,Galego Fernandez N,et al. Structure-prop erties relationship for resols with different formaldehyde/phenol molar ratio. Polymer,1999,40(13):3867~3875 [6] Knop A,Pilato L A. Phenolic resins[M]. Berlin:Spring,1985 [7] Astarloa-Aierbe G,Echeverria J M,Riccardi C C,et al. Influence of the temperature on the formation of a phenolic resol resin catalyzed with ami ne[J]. Polymer,2002,43(8)∶2239~2243 [8] 于振和. S-176酚醛树脂及其塑料[J]. 工程塑料应用,1986,(2):13 ~15 Yu Zhenhe. Alcohol-soluble phenolic resin and its plastics[J]. Engineering P lastics Application,1986,(2):13~15(in Chinese)