Effect of sulfate-reduced bacteria on corrosion and electrochemical behaviors of LY6 Al alloy

School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China

摘要

摘要: 用开路电位法,动电位扫描极化法和电化学交流阻抗频谱法(EIS)研究了LY6在不含硫酸盐还原菌(SRB)的无菌溶液和含SRB的有菌溶液中的电化学行为.结果表明SRB加速了LY6的腐蚀,且动态挂片的腐蚀速率大于静态挂片的腐蚀速率,铝合金开路电位随试验时间的增加而负移,有菌溶液中负移0.26V(SCE),无菌溶液中负移0.16V(SCE).从阳极极化曲线上观察到表观点蚀电位范围为-0.6~0.2V(SCE).电化学阻抗谱表明随着菌液培养时间的增加,极化电阻减小.
- 硫酸盐还原细菌 /
- 铝合金 /
- 电化学阻抗谱
Abstract: The open circuit potential, potentiodynamic scanning polarization and electrochemical impedance spectroscopy (EIS) were employed to analyze the corrosion behaviors of LY6 Al alloy in solutions with and without sulfate reduced bacteria(SRB).It was showed that SRB accelerated the corrosion rate of LY6 Al alloy, and the corrosion rate of dynamic test sample was larger than that of static test sample. The open circuit potential shifted negatively with the time. The shifted values were 0.26V(SCE)and 0.16V (SCE) in solution with and without SRB,respectively. The range of apparent pitting potential obtained from anodic polarization was -0.6~0.2V(SCE). It was found that polarization resistance decreased with the time based on EIS results.
- sulfate-reducing bacteria /
- aluminium alloys /
- electrochemical impedance spectorscopy

HTML全文

参考文献(1)

[1] Inverson W P, Research on the mechanisms of anaerobic corrosion[J]. International Biodeterioration & Biodegradation, 2001, 47(2):63~70 [2] 赖晓春.微生物腐蚀研究进展[J].材料保护,1986,19(6):4~8 Lai Xiaochun. Development of microbiologically induced corrosion study[J]. Materials Protection,1986,19(6):4~8(in Chinese) [3] Eashwar M, Chandrasekaran P, Subramanian G, et al. Microbiologically influenced corrosion of steel during putrefaction of seawater:evidence for a new mechanism[J].Corrosion, 1993,49,2:108~113 [4]Honneysett D G, Burgh W D. Microbiologically corrosion control in a cooling water system[J]. MP 24,1985,10:34~38 [5]Cabrol S. Modeling of corrosion pit growth on the 2024 T351 aluminum alloy in chloride medium[J]. Annales de Chimie Science des Materiaux, 1999,24(4-5):237~311 [6]Pickering H W. Corrosion and electrochemical behaviors of 7075 alloy in water solutions[J]. Corrosion Science, 1989, 29(275):325~330 [7]Little B J, Wagner P A, Ray R I. Microbiologically influenced corrosion in copper and nickel seawater [J]. Marine Technology Society,1990,24(3):10~17 [8]Hedrick H G. Reviews:microbiologically influenced corrosion[J]. Materials Protection, 1970,9(1):27~30 [9] 李松梅,刘建华,杨应广. A3钢在厌氧环境中的新型缓蚀剂性能研究 . 北京航空航天大学学报,2000,26(6):624~627 Li Songmei, Liu Jianhua, Yang Yingguang. Inhibitors for microbiologically induced corrosion of A3 steel in anaerobic enivonment[J]. Jounrnal of Beijing University of Aeronautics and Astornautics, 2000,26(6):624~627(in Chinese) [10] Starosvetsky J, Armon R. MIC of storage tank aluminum floating roffs during hydrotest[J]. Materials Selection & Design,2002,4:50~54 [11] 刘永辉.金属腐蚀学原理[M].北京:航空工业出版社,1993 Liu Yonghui.The theory of metal corrosion[M].Beijing:Aeronautics Industy Press,1993(in Chinese)