热处理对纳米氧化锆热障涂层热物性的影响

周春根 王娜 宫声凯 徐惠彬

周春根, 王娜, 宫声凯, 等 . 热处理对纳米氧化锆热障涂层热物性的影响[J]. 北京航空航天大学学报, 2004, 30(10): 949-952.
引用本文: 周春根, 王娜, 宫声凯, 等 . 热处理对纳米氧化锆热障涂层热物性的影响[J]. 北京航空航天大学学报, 2004, 30(10): 949-952.
Zhou Chungen, Wang Na, Gong Shengkai, et al. Effect of thermal treatment on thermal diffusivity of nanostructured zirconia coating[J]. Journal of Beijing University of Aeronautics and Astronautics, 2004, 30(10): 949-952. (in Chinese)
Citation: Zhou Chungen, Wang Na, Gong Shengkai, et al. Effect of thermal treatment on thermal diffusivity of nanostructured zirconia coating[J]. Journal of Beijing University of Aeronautics and Astronautics, 2004, 30(10): 949-952. (in Chinese)

热处理对纳米氧化锆热障涂层热物性的影响

基金项目: 国家自然科学基金资助项目(50176005)
详细信息
    作者简介:

    周春根 (1964-),男,江西吉安人,教授, cgzhou@buaa.edu.cn.

  • 中图分类号: TG 174

Effect of thermal treatment on thermal diffusivity of nanostructured zirconia coating

  • 摘要: 采用大气等离子喷涂(APS)在GH33基体上制备了氧化锆纳米结构涂层,运用X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电镜(TEM)和拉曼光谱(RS)等分析手段对原料粉末和涂层的显微结构、相组成进行了观察和确定,分别利用激光脉冲技术测量了热处理前后涂层的热扩散率.实验结果表明,等离子喷涂氧化锆纳米涂层颗粒分布在65~110nm之间,大于原料粉末的40~70nm,涂层主要由亚稳四方相氧化锆组成.1050℃下热处理34h后,涂层的热扩散率从制备态的2.15×10-3~2.75×10-3cm2/s升高到2.65×10-3~3.25×10-3cm2/s.

     

  • [1] Rhys-Jones T N,Toriz F C. Thermal barrier coatings for turbine applic ations in aero engines[J]. High Temperature Technology, 1989, 7(1):73~81 [2]Gell M. Application opportunities for nanostructured materials and coatings[J]. Materials Science and Engineering, 1995, A204(1-2):246~251 [3]Kear B H,Skaudan G. Thermal spray processing of nanoscale materials . Nanostructured Materials, 1997, 8(6):765~769 [4]Lima R S, Kucuk A, Berndt C C. Integrity of nanostructured partially stabilized zirconia after plasma spray processing[J]. Materials Science and Engineering, 2001, A313(1-2):75~82 [5]Moelle C, Werner M, Szücs F, et al. Specific heat of single-, poly- and nanocrystalline diamond[J]. Diamond and Related Materials, 1998, 7(4-5):499~503 [6]Khor K A, Gu Y W. Thermal properties of plasma-sprayed functionally graded thermal barrier coatings[J]. Thin Solid Films, 2000, 372(1-2):104~113 [7]Moon J Y, Choi H S, Kim H J, et al. The effects of heat treatment on the phase transformation behavior of plasma-sprayed stabilized ZrO2 coatings[J]. Surface and Coatings Technology, 2002, 155(1):1~10
  • 加载中
计量
  • 文章访问数:  2973
  • HTML全文浏览量:  197
  • PDF下载量:  2
  • 被引次数: 0
出版历程
  • 收稿日期:  2004-04-28
  • 网络出版日期:  2004-10-31

目录

    /

    返回文章
    返回
    常见问答