Effects of thickness and environmental factors on conductivity of composite coatings
-
摘要: 为了给数字化刻铣曲面频率选择表面(FSS)结构的制作和加工提供参考和依据,对比研究了含片状银粉颗粒的聚氨酯基和环氧树脂基2种复合导电涂层的基本性能,并通过环境加速试验,重点研究了温度、湿度以及腐蚀气氛对2种导电涂层的界面强度、微观结构和导电性能的影响.通过电桥法测量涂层表面电阻的变化,并通过扫描电境观察环境试验前后,涂层表面和剖面的微观结构和形貌变化.试验结果表明:聚氨酯基涂层的综合性能优于环氧树脂基涂层;在实验所涉及的参数变化范围内,环境因素对2种涂层与基体的界面结合影响不大,但对其导电性能的影响比较明显.环境因素对导电性能的削弱作用,源于相应过程中导电涂层的微观结构损伤.Abstract: To provide information for the manufacture and application of digital processing frequency selective surface(FSS), the properties of two conductive composite coatings consisting of silver flakes and resin matrix were contrastively investigated. With environmental accelerated test, attention was focused on the effects of environmental factors including temperature, humidity and corrosive atmosphere on their adhesion, microstructure and conductivity. Variation of their surface resistance was measured by bridge method,and their microstructure and pattern change of section and surface were observed before and after environmental test with SEM. The over-all properties of the polyurethane matrix composite coating is better than that of the epoxy resin matrix coating for the two coatings containing silver flakes. The effects of environmental factors on conductivity of the two coatings are obvious, though no appreciable influence on adhesion can be identified in experimental scope and parameter variation range. The negative effect of environmental factors on conductivity is attributed to the micro-damages occurred within the microstructures of the coatings.
-
Key words:
- coats /
- conductivity /
- composite coatings /
- adhesion /
- microstructure /
- environmental impact
-
[1] Gresham R M．EMI/RFI shielding of plastics[J]. Plating and Surface Finishing, 1988, (2):63~69 [2] 涂铭旌.电磁波屏蔽涂料及其制备方法 .中国专利:1200390,1998-12-02 Tu Mingjing. Electromagnetic shielding coatings and its preparation method .China Patent:1200390, 1998-12-02(in Chinese) [3] 吕明云.复杂曲面FSS雷达罩加工系统及工艺方法研究 .北京:北京航空航天大学航空科学与工程学院,2004 Lü Mingyun. Processing system and technique for complex curved FSS of radome . Beijing:School of Aviation Science & Engineering, Beijing University of Aeronautics and Astronautics,2004(in Chinese) [4] 雀部博之.导电高分子材料[M].北京:科学出版社,1989 Quebu Bozhi. Conductive high polymer[M]. Beijing:Science Press,1989(in Chinese) [5] 林 硕,李志章,吴年强.电磁屏蔽导电复合涂料[J].材料导报,1996 (3):72~76 Lin Shuo, Li Zhizhang, Wu Nianqiang. Conductive composite coatings for electromagnetic shielding[J]. Materials Review,1996,3:72~76(in Chinese) [6] Bueche. Electrical resistivity of conducting particles in an insulating matrix[J]. Journal of Applied Physics,1972,43(11):4837 [7] 范太炳.特种胶粘剂[M].北京:科学出版社,1992.145 Fan Taibing. Special adhesives[M].Beijing:Science Press,1992.145(in Chinese) -
点击查看大图
计量
- 文章访问数: 2848
- HTML全文浏览量: 75
- PDF下载量: 715
- 被引次数: 0
下载: