北京航空航天大学学报 ›› 2005, Vol. 31 ›› Issue (10): 1096-1100.

LPA对UPR收缩率和力学性能的影响

孙志杰¹, 薛忠民², 杨博¹, 张佐光¹

1. 北京航空航天大学材料科学与工程学院, 北京 100083;
2. 北京玻璃钢研究设计院, 北京 102101

收稿日期:2004-06-08 出版日期:2005-10-31 发布日期:2010-09-20
作者简介:孙志杰(1951-),男,河北肃宁人,教授, zhjsun@263.net.

Effect of low profile additives on the shrinkage and mechanical properties of unsaturated polyester

Sun Zhijie¹, Xue Zhongmin², Yang Bo¹, Zhang Zuoguang¹

1. School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China;
2. Beijing FRP Research & Design Institute, Beijing 102101, China

Received:2004-06-08 Online:2005-10-31 Published:2010-09-20

摘要/Abstract

摘要： 针对不饱和聚酯树脂(UPR,Unsaturated Polyester Resin)收缩率高和脆性大的缺点,研究了加入两种低轮廓添加剂(LPA,Low Profile Additives)——聚醋酸乙烯酯类的LPA-4016和聚苯乙烯类的LPA-7310——对UPR浇注体的体积收缩率和力学性能的影响,分析了两种体系的相结构转变及不同的低收缩控制机理,LPA-4016主要是通过在LPA颗粒相周围形成许多均匀分散的空隙来抵消树脂的固化收缩;而LPA-7310则主要是通过自身充分膨胀来抵消树脂的固化收缩.结果表明,LPA-4016对UPR的收缩控制存在一个较合适的加入量范围,且与LPA-7310相比,其可改善UPR的脆性,提高冲击强度,但两者都会降低UPR的拉伸强度.

Abstract: In order to reduce the high shrinkage ratio and great brittleness of UPR(unsaturated polyester resin), two kinds of LPA(low profile additives), which are LPA-4016 of polyvinyl acetate and LPA-7301 of polystyrene, are added into UPR cast separately. The effects of LPA on the shrinkage rate and mechanical properties of UPR cast are studied, and then the phase structure transitions of these two systems and their different control mechanisms of low shrinkage rate are analyzed. For LPA-4016, it is by formatting amounts of uniform and disperse voids around the LPA phase to buck the shrinkage during resin cure; while for LPA-7310, this is realized primarily by the sufficient expansion of LPA itself. The results show that there exists an optimal quantity for LPA-4016 to reduce shrinkage rate of UPR, and it can improve the brittleness of UPR and increase its impact strength in contrast with LPA-7310. But both of them tend to reduce the tensile strength of UPR.

中图分类号:

TB 32
TB 33

孙志杰, 薛忠民, 杨博, 张佐光. LPA对UPR收缩率和力学性能的影响[J]. 北京航空航天大学学报, 2005, 31(10): 1096-1100.

Sun Zhijie, Xue Zhongmin, Yang Bo, Zhang Zuoguang. Effect of low profile additives on the shrinkage and mechanical properties of unsaturated polyester[J]. JOURNAL OF BEIJING UNIVERSITY OF AERONAUTICS AND A, 2005, 31(10): 1096-1100.

参考文献

[1] 邱桂杰,王侃．低收缩添加剂对聚酯树脂固化的影响[J] 璃钢/复合材料,2003,(2):27~29 Qiu Guijie, Wang Kan. Study on the effects of low profile additives on unsaturated polyester curing [J] Fiber Reinforced Plastics/Composite Materials, 2003,(2):27~29 (in Chinese) [2] 杨睿,潘安徽,赵世崎．不饱和聚酯树脂的原位同时增韧和降收缩研究．高分子材料科学与工程,2003,19(7):140~142 Yang Rui, Pan Anhui, Zhao Shiqi. Simultaneously in-situ toughening and low shrinking of unsaturated polyester resin [J] Polymer Materials Science and Engineering, 2003,19(7):140~142(in Chinese) [3] Li W, Lee L J. Low temperature cure of unsaturated polyester resins with thermoplastic additives I dilatometry and morphology study [J] Polymer, 2000, 41(2):685~696 [4] Wang Kan. The effect of low profile additives on unsaturated polyester resins during curing at low/medium temperature:shrinkage behavior study [J] Key Engineering Materials, 2003,(249):351~354 [5] Suspene Laurent, Fourquier Dominique, Yang YeongShow. Application of phase diagrams in the curing of unsaturated polyester resins with low-profile additives [J] Polymer, 1991,32(9):1593~1604 [6] Huang Yanjyi. Effects of poly(vinyl acetate) and poly(methyl methacrylate) low-profile additives on the curing of unsaturated polyester resins II. Morphological changes during cure[J] Journal of Applied Polymer Science, 1995, 55(1):323~342 [7] Li W, Lee L J. Low temperature cure of unsaturated polyester resins with thermoplastic additives III. Modification of polyvinyl acetate for better shrinkage control [J] Polymer, 2000,41:711~717 [8] Li W, Lee L J. Low temperature cure of unsaturated polyester resins with thermoplastic additives II. Structure formation and shrinkage control mechanism [J] Polymer, 2000,41:697~710 [9] Cao X, Lee L J. Effect of co-promoter and secondary monomer on shrinkage control of unsaturated polyester(UP)/styrene/low-profile additive(LPA) systems cured at low temperatures[J] Journal of Applied Polymer Science, 2001,82(11):738~749 [10] Huang Yanjyi. Effects of low-profile additives on volume shrinkage characteristics in the cure of unsaturated polyester resins . Annual Technical Conference-ANTEC, Conference Proceedings . 1995,1:897~901 [11] 冯青平,薛忠民,曾鸿鸣．低收缩添加剂的研究进展及发展方向[J] 璃钢/复合材料,2001,(1):46~49 Feng Qingping, Xue Zhongmin, Zeng Hongming. LPA research progress and developing trend [J] Fiber Reinforced Plastics/Composites Materials, 2001,(1):46~49(in Chinese) [12] 冯青平,薛忠民,熊传溪．低收缩相态结构的研究综述[J] 璃钢/复合材料,2000,(4):43~46 Feng Qingping, Xue Zhongmin, Xiong Chuanxi. Study of LPA phase structure [J] Fiber Reinforced Plastics/Composites Materials, 2000,(4):43~46(in Chinese) [13] 王侃,王继辉,薛忠民,等．国外低轮廓UPR固化收缩控制研究发展动态[J] 璃钢/复合材料,2003,(4):34~37 Wang Kan, Wang Jihui, Xue Zhongmin, et al. Study progress in shrinkage control of low profile unsaturated polyester resin during cure [J] Fiber Reinforced Plastics/Composites Materials, 2003,(4):34~37(in Chinese) [14] Atikins K E, Rex G C. The low profile effect:morphology and internal pigmentation [J] Part-II, SPI Session 6-C, 1993 [15] 何曼君,陈维孝,董西侠．高分子物理[M] 海:复旦大学出版社,1983.223~224 He Manjun, Chen Weixiao, Dong Xixia. High polymer physics [M] Shanghai:Fudan University Press, 1983.223~224 (in Chinese)