Microstructure and affecting factors of epoxy resin cured by electron beam radiation

Li Yubin1, Zhang Zuoguang1, Sun Zhijie1, Yang Jialing2   

  1. 1. School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China;
    2. School of Aeronautic Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China
  • Received:2006-10-20 Online:2007-08-31 Published:2010-09-17

摘要: 采用扫描电镜对不同固化时间下电子束固化环氧树脂的微观结构进行观察和分析,探讨其形成过程,并研究了树脂分子结构、相对分子质量、树脂体系组分及辐射条件对微观结构的影响. 实验结果表明,环氧树脂经电子束固化后形成片层结构,树脂分子结构和分子量对其固化微结构的影响不大;不同结构、分子量的环氧树脂电子束固化过程中均会经历预聚体结构—圆片网络—圆片形成—圆片增长的生长过程,故其微观结构都呈现圆片状形貌;随着辐射剂量的增加,圆片逐渐增大;存在最佳引发剂用量,使圆片尺寸达到最小.

Abstract: A scanning electron microscope (SEM) was used to observe the microstructures of cured samples after different cure time. The formation mechanism of microstructure was analyzed. The effects of molecular structure and molecular weight of epoxy resin, resin component, and radiation condition on the microstructure were also researched. The results show that the cure zone of epoxy resin consists of lamellae, and the resin molecular structure and weight have little effect on the cured microstructure. Under the electron beam radiation, epoxy resins with different structures or molecular weights all form prepolymer at first, then the prepolymer grows into network. With the radiation time increases, the network grows larger and the circular sheet forms finally. With the increasing of radiation dosage, the size of circular sheet increases. And there exists an optimum content of initiator, which makes the size of circular sheet reach the minimum.