留言板

尊敬的读者、作者、审稿人, 关于本刊的投稿、审稿、编辑和出版的任何问题, 您可以本页添加留言。我们将尽快给您答复。谢谢您的支持!

姓名
邮箱
手机号码
标题
留言内容
验证码

稀土元素对Al-Ni-Gd-Y合金晶化行为的影响

宋洪海 段辉平 马朝利 张 涛

宋洪海, 段辉平, 马朝利, 等 . 稀土元素对Al-Ni-Gd-Y合金晶化行为的影响[J]. 北京航空航天大学学报, 2009, 35(5): 540-543.
引用本文: 宋洪海, 段辉平, 马朝利, 等 . 稀土元素对Al-Ni-Gd-Y合金晶化行为的影响[J]. 北京航空航天大学学报, 2009, 35(5): 540-543.
Song Honghai, Duan Huiping, Ma Chaoli, et al. Effects of rare-earth (RE) elements on crystallization behavior of Al-Ni-Gd-Y amorphous alloy[J]. Journal of Beijing University of Aeronautics and Astronautics, 2009, 35(5): 540-543. (in Chinese)
Citation: Song Honghai, Duan Huiping, Ma Chaoli, et al. Effects of rare-earth (RE) elements on crystallization behavior of Al-Ni-Gd-Y amorphous alloy[J]. Journal of Beijing University of Aeronautics and Astronautics, 2009, 35(5): 540-543. (in Chinese)

稀土元素对Al-Ni-Gd-Y合金晶化行为的影响

基金项目: 国家重点基础研究发展计划资助项目(2007CB613900); 国家自然科学基金资助项目(50631010,50771006); 长江学者和创新团队发展计划资助项目(IRT0512)
详细信息
    作者简介:

    宋洪海(1983-),男,广西柳州人,硕士生,couloursea@126.com.

  • 中图分类号: TG 13

Effects of rare-earth (RE) elements on crystallization behavior of Al-Ni-Gd-Y amorphous alloy

  • 摘要: 利用差示扫描量热仪(DSC)、X射线衍射(XRD)、透射电镜(TEM)研究了稀土元素(RE)对Al-Ni-Gd-Y非晶合金晶化行为的影响.Al-Ni-Gd-Y非晶合金的初始晶化温度随着稀土元素含量的增加而升高.在Al(88-x)Ni6Gd6Y x ( x =1,2,3,4)系中,随着Y含量的增加,初始晶化产物由面心立方Al(fcc-Al)变成为fcc-Al+Al3Gd/Al3Y+未知相.研究了热处理工艺对Al86Ni8Gd3Y3合金力学性能的影响,其中,当Al86Ni8Gd3Y3在568K下保温10min时,其显微硬度及韧性较高,析出尺寸为1~3nm的fcc-Al纳米晶颗粒.

     

  • [1] Klement W, Willens R, Duwez P. Non-crystalline structure in solidified gold- silicon alloy [J]. Nature,1960,187:869 [2] Inoue A, Yamamoto M , Kimura H M , et al. Ductile aluminum-base amorphous alloys with two separate phases[J]. J Mater Sci Lett, 1987 ,6(1):194-196 [3] He Y, Poon S, Shiflet G. Synthesis and properties of metallic glasses that contain aluminum [J]. Science, 1988,241:1640-1642 [4] He Y, Dougher G. Strength in Al-Ni-Fe-Gd alloys[J]. Acta Metall Mater, 1993,41(2):337-343 [5] Greer A L, Materials science- confusion by design[J]. Nature, 1993, 366:303-304 [6] Kawamura Y, Mano H, Inoue A. Nanocrystalline aluminum bulk alloys with a high strength of 1420MPa produced by the consolidation of amorphous powders[J]. Scripta Mater, 2001,44(8-9):1599-1604 [7] Inoue A. Amorphous, nanoquasicrystalline and nanocrystalline alloys in Al-based systems[J]. Prog Mater Sci, 1998,43(5): 365-520 [8] Chen H, He Y, Shiflet G, et al. Mechanical properties of partially crystallized aluminum based metallic glasses[J]. Scripta Metall Mater, 1991,25(6):1421-1424 [9] Inoue A, Ohtera K, Tsai A P, et al. Glass transition behavior of Al-Y-Ni and Al-Ce-Ni amorphous alloys[J]. Jpn J Appl Phys, 1988,27(3):280-282 [10] Saini S, Zaluska A, Altounian Z. Effect of glass short-range order on crystallization onset in Al-Y-Ni glasses[J]. J Non-Cryst Solids, 1999, 250-252:714-718
  • 加载中
计量
  • 文章访问数:  3249
  • HTML全文浏览量:  1
  • PDF下载量:  1209
  • 被引次数: 0
出版历程
  • 收稿日期:  2008-08-10
  • 刊出日期:  2009-05-31

目录

    /

    返回文章
    返回
    常见问答