喷涂功率对纳米热障涂层组织及性能的影响

孙友贝; 周春根

喷涂功率对纳米热障涂层组织及性能的影响

北京航空航天大学材料科学与工程学院, 北京 100191

详细信息

作者简介:
孙友贝(1987-),男,山东济宁人,硕士生,syb@mse.buaa.edu.cn.

中图分类号: TG174
计量
- 文章访问数: 1247
- HTML全文浏览量: 187
- PDF下载量: 531
- 被引次数: 0
出版历程
- 收稿日期: 2012-10-24
- 网络出版日期: 2013-09-30

Effect of spraying power on microstructure and property of nanostructured thermal barrier coatings

School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100191, China

摘要

摘要: 采用扫描电子显微镜(SEM,Scanning Electron Microscopy)、X射线衍射(XRD, X-Ray Diffraction)等方法研究了大气等离子喷涂功率对纳米Y₂O₃部分稳定的ZrO₂ (YSZ,Yttria Stabilized Zirconia)热障涂层组织结构及热震性能的影响.结果表明,不同功率下制备的陶瓷层包含熔融相和未熔相,未熔相中存有纳米晶粒,相组成为四方相ZrO₂.随着功率的增加,涂层的纳米区域逐渐减少,孔隙率逐渐降低,热震寿命先增加后减少.涂层失效位置位于靠近TGO(Thermally Grown Oxide)处的陶瓷层中.
- 纳米YSZ /
- 组织结构 /
- 热震性能
Abstract: Effect of air plasma spraying power on microstructure and thermal shock of nanostructured yttria stabilized zirconia (YSZ) thermal barrier coatings was investigated by scanning electron microscopy (SEM) and X-ray diffraction (XRD). It was found that there were two regions of melted phases and non-molten phases for the ceramic top coating under different power, non-molten phases included the nanosized grains, and phase composition was metastable tetragonal zirconia. With the increase in power, the area of nanosized grains gradually decreased, the porosity of the coating gradually reduced, and the life of the coating increased first and then decreased. The coating failure position was located at the ceramic top coating close to thermally grown oxide(TGO).
- nanostructured YSZ /
- microstructure /
- thermal shock

HTML全文

参考文献(1)

[1] Goward G W.Progress in coatings for gas turbine airfoils[J].Surface and Coatings Technology,1998,108/109:73-79 [2] Beele W,Marijnissen G,van Lieshout A.The evolution of thermal barrier coatings-status and upcoming solutions for today-s key issues[J].Surface and Coatings Technology,1999,120/121:61-67 [3] Padture N P,Gell M,Jordan E H.Thermal barrier coatings for gas-turbine engine applications[J].Science,2002,296:280-284 [4] Zhou Chungen,Wang Na,Wang Zhenbo,et al.Thermal cycling life and thermal diffusivity of a plasma-sprayed nanostructured thermal barrier coating[J]. Scripta Materialia,2004,51(10):945-948 [5] Liu Chunbo,Zhang Zhimin,Jiang Xianliang,et al.Comparison of thermal shock behaviors between plasma-sprayed nanostructured and conventional zirconia thermal barrier coatings[J].Transactions of Nonferrous Metals Society of China,2009,19:99-107 [6] Zhou Chungen,Wang Na,Xu Huibin.Comparison of thermal cycling behavior of plasma-sprayed nanostructured and traditional thermal barrier coatings[J].Materials Science and Engineering A,2007,452/453:569-574 [7] Lima R S,Marple B R.Nanostructured YSZ thermal barrier coatings engineered to counteract sintering effects[J].Materials Science and Engineering A,2008,485(1/2):182-193 [8] Khan N A,Lu J.Behavior of air plasma sprayed thermal barrier coatings,subject to intense thermal cycling[J].Surface and Coatings Technology,2003,16:37-43 [9] Wang W Q,Sha C K,Sun D Q,et al.Microstructural feature,thermal shock resistance and isothermal oxidation resistance of nanostructured zirconia coating[J]. Materials Science and Engineering A,2006,424:1-5 [10] Liang Bo,Ding Chuanxian.Thermal shock resistances of nanostructured and conventional zirconia coatings deposited by atmospheric plasma spraying[J].Surface and Coatings Technology,2005,197:185-192 [11] Lima R S,Kucuk A,Berndt C C.Integrity of nanostructured partially stabilized zirconia after plasmas pray processing[J].Materials Science and Engineering,2001,313:75-82 [12] Huang Hui,Liu Chao,Ni Liyong,et al.Evaluation of microstructural evolution of thermal barrier coatings exposed to Na₂SO₄ using impedance spectroscopy[J].Corrosion Science,2011,4:1369-1374 [13] Ajdelsztajn L,Picas J A,Kim G E,et al.Oxidation behavior of HVOF sprayed nanocrystalline NiCrAlY powder[J].Materials Science and Engineering A,2002,338:33-43 [14] Lee C H,Kim H K,Choi H S,et al.Phase transformation and bond coat oxidation behavior of plasma-sprayed zirconia thermal barrier coating[J].Surface and Coatings Technology,2000,124:1-12 [15] Rabiei A,Evans A G.Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings[J].Acta Mater,2000,48:3963-3976 [16] Miller R A,Lowell C E.Failure mechanisms of thermal barrier coatings exposed to elevated temperatures[J].Thin Solid Films,1982,95:265-273 [17] Khor K A,Jana S.Pulsed laser processing of plasma sprayed thermal barrier coatings[J].Journal of Materials Processing Technology,1997,66:4-8 Kuroda S,Clyne T W.The quenching stress in thermally sprayed coatings[J].Thin Solid Films,1991,1:49-66