Study on corrosion resistance of aircraft conduit connector at simulated service environment

  • Received Date: 07 Nov 2003
  • Publish Date: 30 Apr 2005
  • Corrosion resistance, airproof property and oilproof property of aircraft conduit connector of Cd-electroplated 45# steel were studied by a conduit connector corrosion experiment system at simulated service environment. Cd-electroplated 45# steel was placed in the solution of 6% NaCl at 90±5℃ for 5 minutes and then in the air at 60±5℃ for 25 minutes. This process was cycled for 200 times. The behaviors of surface corrosion and stress corrosion of the connectors were evaluated and the corrosion mechanism was investigated. It was not found that 45# steel was corroded in No.10 fuel. Only slight corrosion was found on the surface of 45# steel at simulated service environment. It was shown that the Cd-electroplated layer as anode plating layer on 45# steel has excellent protection to the matrix metal. The result of the experiment under the bending stress of 0.85σs indicated that the Cd-coated 45# steel has good corrosion resistance to SCC. Galvanic corrosion of LF2-M coupled with 45# steel was investigated. It was found that the galvanic current of the couple of LF2-M coupled with 45# steel is very low. The mean galvanic corrosion current is 0.185μA/cm2. It was demonstrated that the conduit of LF2-M and its connector of 45# steel can be coupled safely.

     

  • [1] cIntyre, Dale R, Moore E. Specified pipe fittings susceptible to sulfide stress cracking[J]. Materials Performance,1996 ,35(1):1~2 [2] Anast M, Jamting A, Bell J, et al. Surface morphology examination of sol-gel deposited TiO2[J]. Thin Solid Films,1994,25(3):303~307 [3] 俊升. 28 MPa导管连接件标准研究[J].航空标准化与质量,1999(4):4~5 Li Junsheng. Study on standard of 28Mpa conduit connector [J]. Aerial Standardization and Quality, 1999(4):4~5(in Chinese) [4] hang Zhenggui. Influence of stress amplitude and corrosive factors on corrosion fatigue life of riveted joints[J]. Journal of Mechanical Strength,2002,23(2):243~245 [5] 永辉. 金属腐蚀学原理[M].北京:航空工业出版社,1993.73~95 Liu Yonghui. Theory of metal corrosion[M].Beijing:Aerial Industry Press, 1993.73~95 (in Chinese) [6] 文海 . 液压导管漏油故障分析及其预防措施[J].液压与气动,2001(12):37~38 Cai Wenhai. Analysis and protection of oil leak hydraulic pressure conduit . Hydraulic Pressure and Pneumatic Technology, 2001(12):37~38 (in Chinese) [7] 传彬. 某新型飞机燃油导管安装不当导致事故隐患[J].飞机事故和失效分析,1993(4):34~35 Pu Chuanbin. Possibility of accident caused by improper fixing oil conduit in a new aeroplane[J]. Aeroplane Accident and Failure Analysis,1993(4):34~35(in Chinese) [8] ellucci F. Galvanic corrosion between nonmetallic composites and metals effect of metal and of temperature[J]. Corrosion, 1991,47(10):42~43
  • Relative Articles

    [1]TIAN Bin, YANG Lichun, MEI Yuan, DANG Jianwu. Unsupervised Single-response Estimation for Integrating In-domain Information Under Large Baselines[J]. Journal of Beijing University of Aeronautics and Astronautics. doi: 10.13700/j.bh.1001-5965.2024.0659
    [2]LIU Yansong, SHI Wenze, LU Chao, ZHANG Qi, TANG Wenbin, ZHANG Lugen. Research on the Influence Law of Ultrasonic Echoes and Quantitative Defect Detection of High-Temperature Stainless Steel with Coil-only EMAT[J]. Journal of Beijing University of Aeronautics and Astronautics. doi: 10.13700/j.bh.1001-5965.2024.0879
    [3]XU J Q,LIN H P,GUO H. Multi-layer wave-shaped topology and thermal design method for aero-electric propulsion motors[J]. Journal of Beijing University of Aeronautics and Astronautics,2024,50(6):1806-1818 (in Chinese). doi: 10.13700/j.bh.1001-5965.2022.0498.
    [4]ZHAO M,JIA H,WU S Q,et al. Mechanical characteristics of flexible connection technology for Mars parachute[J]. Journal of Beijing University of Aeronautics and Astronautics,2024,50(12):3815-3824 (in Chinese). doi: 10.13700/j.bh.1001-5965.2022.0932.
    [5]LI Peiyuan, CAI Qiaoyan, LI Zengshan, FENG Jiahe. Damage tolerance analysis and research on reusable launch vehicle connection structures[J]. Journal of Beijing University of Aeronautics and Astronautics. doi: 10.13700/j.bh.1001-5965.2024.0221
    [6]YU Y B,HE Z Q,HE X F,et al. Rotating bending fatigue life prediction of bearing steel based on damage mechanics[J]. Journal of Beijing University of Aeronautics and Astronautics,2024,50(8):2585-2594 (in Chinese). doi: 10.13700/j.bh.1001-5965.2022.0639.
    [7]LUO Yanyan, QI Qiaoshen, WANG Yongpeng, WU Xiongwei. Fretting wear test and performance degradation model of electrical connector under step random vibration[J]. Journal of Beijing University of Aeronautics and Astronautics. doi: 10.13700/j.bh.1001-5965.2024.0350
    [8]LIU D J,TIAN G,LI Y L,et al. Research on pre-corrosion fatigue properties of 2195 Al-Li alloys in 30% HNO3[J]. Journal of Beijing University of Aeronautics and Astronautics,2024,50(4):1129-1137 (in Chinese). doi: 10.13700/j.bh.1001-5965.2022.0445.
    [9]GUO Y,LIU D J,CHANG X L,et al. Corrosion behavior of 2195-T8 aluminum-lithium alloy with artificial defects in 30% HNO3[J]. Journal of Beijing University of Aeronautics and Astronautics,2024,50(3):896-903 (in Chinese). doi: 10.13700/j.bh.1001-5965.2022.0344.
    [10]ZHANG Q S,LI D Q,LIAN X X. Study of corrosion and hydrogen evolution risk of waded lithium ion-battery[J]. Journal of Beijing University of Aeronautics and Astronautics,2024,50(7):2083-2092 (in Chinese). doi: 10.13700/j.bh.1001-5965.2022.0617.
    [11]YAO X Y. Influence of mistuning bolted joints on dynamic characteristics of thin-walled cylinder[J]. Journal of Beijing University of Aeronautics and Astronautics,2023,49(5):1238-1246 (in Chinese). doi: 10.13700/j.bh.1001-5965.2021.0468.
    [12]WANG Y D,SUN Y F,LEI D Y,et al. Thermal oxidation reliability and structure optimization of thin film thermocouple[J]. Journal of Beijing University of Aeronautics and Astronautics,2023,49(4):943-948 (in Chinese). doi: 10.13700/j.bh.1001-5965.2021.0318.
    [13]WANG Z J,YAO J,XIONG J Z,et al. Experimental research on erosion of Q345 steel under two-phase flow condition[J]. Journal of Beijing University of Aeronautics and Astronautics,2023,49(4):891-899 (in Chinese). doi: 10.13700/j.bh.1001-5965.2021.0357.
    [14]LI Xing, LI Zeng-shan, DENG Fan-chen, NIE Lei, ZHANG Tian. Sub-model Based Failure Analysis of Composite Hybrid Joint Structure[J]. Journal of Beijing University of Aeronautics and Astronautics. doi: 10.13700/j.bh.1001-5965.2023.0555
    [15]ZHANG S,HE Y T,NI B,et al. Effect of nitrate on exfoliation corrosion of 2A12-T4 aluminum alloy under full-immersion corrosion condition[J]. Journal of Beijing University of Aeronautics and Astronautics,2023,49(6):1372-1382 (in Chinese). doi: 10.13700/j.bh.1001-5965.2021.0473.
    [16]BI Y P,ZHANG T,HE Y T,et al. Corrosion and fatigue life prediction of aircraft typical lap structures based on life envelope[J]. Journal of Beijing University of Aeronautics and Astronautics,2023,49(8):2200-2206 (in Chinese). doi: 10.13700/j.bh.1001-5965.2022.0604.
    [17]SHI W Z,HUANG Q K,LU C,et al. Application of pulse compression technique in steel plate corrosion detection with SH guided wave EMATs[J]. Journal of Beijing University of Aeronautics and Astronautics,2023,49(2):324-334 (in Chinese). doi: 10.13700/j.bh.1001-5965.2021.0229.
    [20]KANG Rui, LIU Haoran, ZHANG Qingyuan, YU Li, ZHAI Guofu. Function oriented belief reliability design and optimization of new torsion spring electrical connectors[J]. Journal of Beijing University of Aeronautics and Astronautics, 2022, 48(9): 1745-1756. doi: 10.13700/j.bh.1001-5965.2022.0323
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article views(3215) PDF downloads(888) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return