Journal of Beijing University of Aeronautics and Astronautics  > 2012  >  38(10): 1380-1383.
Wang Wenbo, Zhou Chungen. Interdiffusion behavior in Nb/α-Ti3Al ternary system[J]. Journal of Beijing University of Aeronautics and Astronautics, 2012, 38(10): 1380-1383. (in Chinese)
Citation: Wang Wenbo, Zhou Chungen. Interdiffusion behavior in Nb/α-Ti3Al ternary system[J]. Journal of Beijing University of Aeronautics and Astronautics, 2012, 38(10): 1380-1383. (in Chinese)
shu

Interdiffusion behavior in Nb/α-Ti3Al ternary system

  • School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100191, China

  • Received Date: 30 Sep 2011
  • Publish Date: 30 Oct 2012
    Abstract
  • The α2 single phase interdiffusion behavior in Ti3Al-Nb ternary system was studied at the temperature of 1 273 K, 1 423 K, 1 573 K, using Ti3Al/Nb single phase diffusion couples. The uniform β-(Ti, Nb) phase was formed in mid of the diffusion couple after 120 hours diffusion annealing in the high temperature. On the contrary, the nonuniform diffusion layers, including Ti3Al(Nb), β-(Ti,Nb) and Nb2Al, were formed in low temperature.The interdiffusion coefficients were calculated by the method of Dayananda, which can evaluate by the concentration dependence in one couple only. The calculation results show that the interdiffusion coefficients of Ti and Al is five order of magnitude larger than Nb, and Nb atoms are considered to occupy Ti sites in Ti3Al, the exchanges with vacancies on Ti sublattice played a leading role in the diffusion of Ti3Al. These results can provide a theoretical basis for the mechanisms of Nb improving the oxidation resistance of Ti3Al.

     

    • FullText(HTML)
  • loading
    • References(16)
  • [1]
    Kim Y W.Microstructural evolution and mechanical properties of a forged gamma titanium aluminide alloy[J].Acta Metallurgica et Materialia,1992,40(6):1121-1134
    [2]
    Liu C T.Recent advances in ordered intermetallics[J].Materials Chemistry and Physics,1995,42(2):77-86
    [3]
    Yamaguchi M,Inui H,Ito K.High-temperature structural intermetallics[J].Acta Materialia,2000,48(1):307-322
    [4]
    Chu M S,Wu S K.Improvement in the oxidation resistance of α2-Ti3A1 by sputtering Al film and subsequent interdiffusion treatment[J].Surface Coating Technology,2004,179(2/3):257-264
    [5]
    Fang Wei,Ko Se Hyun,Hashimoto Hitoshi.High temperature oxidation behavior of Ti3Al-Nb alloys prepared by pulse discharge sintering[J].Material Science and Engineering:A,2002,329/330/331:708-713
    [6]
    Wang Yanhang,Lin Junpin,He Yuehui,et al.Reaction mechanism in high Nb containing TiAl alloy by elemental powder metallurgy[J].Transactions of Nonferrous Metals Society of China,2006,16(4):853-857
    [7]
    王兴军,常海威,雷明凯.Nb合金化γ-TiAl的氧化热力学理论分析[J].金属学报,2001,37(8):811-814 Wang Xingjun,Chang Haiwei,Lei Mingkai.Thermodynamic aspects of oxidation for Nb alloying γ-TiAl intermatallic compounds[J].Acta Matallurgica Sinica,2001,37(8):811-814(in Chinese)
    [8]
    Rüsing J,Herzig C.Concentration and temperature dependence of titanium self-diffusion and interdiffusion in the intermetallic phase Ti3Al[J].Intermetallics,1996,4(8):647-657
    [9]
    Brever J,Wilger T,Friesel M,et al.Interstitial and substitutional diffusion of metallic solutes in Ti3Al[J].Intermetallic,1999,7(3/4):381-388
    [10]
    Dayananda M A.Average effective interdiffusion coefficients and matano plane composition[J].Metallurgical and Materials Transactions A,1996,27(9):2504-2509
    [11]
    Dayananda M A.A new analysis for the determination of ternary interdiffusion coefficients from a single diffusion couple[J].Metallurgical and Materials Transactions A,1999,30(3):535-543
    [12]
    Tororic P C,Dayananda M A.Interdiffusion and diffusion structure development in selected refractory metal silicides[J].Materials Science and Engineering:A,1999,261(1/2):64-77
    [13]
    Cermak J,Rothova V.Concentration dependence of ternary interdiffusion coefficients in Ni3Al/Ni3Al-X couples with X=Cr,Fe,Nb and Ti[J].Acta Materialia,2003,51(15):4411-4421
    [14]
    Garimella N,Ode M,Ikeda M.Effects of Ir or Ta alloying addition on interdiffusion of L12-Ni3Al[J].Intermetallics,2008,16(9):1095-1103
    [15]
    Yao Dengzun,Yang Junying,Gong Weiyan,et al.Interdiffusion behavior between Nb and MoSi2 intermetallic compound[J].Materials Science and Engineering:A,2010,527(26):6787-6793
    [16]
    Wei Haixia,Gong Weiyang,Huang Sheng,et al.Single-phase interdiffusion in the Ni3Al-Mo ternary system[J].Scripta Materialia,2011,64(1):53-56
    • Relative Articles
    • Supplements(0)
    • Cited By
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索
    Get Citation
    PDF
    XML

    Article Metrics

    Article views(1890) PDF downloads(538) Cited by()
    Proportional views
    Related

    Copyright © Journal of Beijing University of Aeronautics and Astronautics

    Address: Editorial Department of Journal of Beijing University of Aeronautics and Astronautics, 37 Xueyuan Road, Haidian District, Beijing Post Code: 100191 Email: jbuaa@buaa.edu.cn

    Supported by: Beijing Renhe Information Technology Co., Ltd.    

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return