| Citation: | WANG Tingting, GU Yizhuo, WANG Shaokai, et al. Characterization on axial thermal conductivity of carbon fiber and its influence factors[J]. Journal of Beijing University of Aeronautics and Astronautics, 2017, 43(9): 1931-1938. doi: 10.13700/j.bh.1001-5965.2016.0757(in Chinese)
|
Two measurement methods for carbon fiber's axial thermal conductivity are compared, which use fiber bundle and unidirectional fiber reinforced composite samples, respectively. The influence of fiber volume fraction and sample thickness on the measurement was discussed. The applicability of the method based on fiber bundle was investigated by testing polyacrylonitrile-based high-strength and high-modulus carbon fibers, and mesophase pitch-based carbon fiber. The relationship between thermal conductivity and microstructure was further discussed. The results indicate that unidirectional composite shows lower axial thermal diffusivity than fiber bundle sample due to the thermal conduction between fiber and polymer matrix in composite. Accurate thermal conductivity can be obtained by using fiber bundle sample, while unidirectional composite sample yields bigger thermal conductivity. For the measurement with unidirectional composite, the calculated thermal conductivity increases with the increase of fiber volume fraction and sample thickness. On the contrary, fiber bundle samples result in stable thermal conductivity which is not affected by fiber volume fraction. Moreover, the thermal conductivity increases in the order of mesophase pitch-based carbon fiber, high-modulus and high-strength carbon fiber. Lower lattice spacing and larger crystallite size leads to bigger thermal conductivity. These results may contribute to the accurate characterization on axial thermal conductivity of carbon fiber and the structural design of highly thermal conductive fiber composite.
| [1] |
DÍAZÁLVAREZ J, OLMEDO A, SANTIUSTE C, et al.Theoretical estimation of thermal effects in drilling of woven carbon fiber composite[J].Materials, 2014, 7(6):4442-4454. doi: 10.3390/ma7064442
|
| [2] |
DONG K, GU B, SUN B.Comparisons of thermal conductive behaviors of epoxy resin in unidirectional composite materials[J].Journal of Thermal Analysis & Calorimetry, 2015, 124(2):1-15. doi: 10.1007/s10973-015-5197-5
|
| [3] |
HAN S, CHUNG D D L.Increasing the through-thickness thermal conductivity of carbon fiber polymer-matrix composite by curing pressure increase and filler incorporation[J].Composites Science & Technology, 2011, 71(16):1944-1952. http://www.sciencedirect.com/science/article/pii/S0266353811003381
|
| [4] |
SCHUSTER J, HEIDER D, SHARP K, et al.Measuring and modeling the thermal conductivities of three-dimensionally woven fabric composites[J].Mechanics of Composite Materials, 2009, 45(2):165-174. doi: 10.1007/s11029-009-9072-y
|
| [5] |
DONG K, LIU K, ZHANG Q, et al.Experimental and numerical analyses on the thermal conductive behaviors of carbon fiber/epoxy plain woven composites[J].International Journal of Heat & Mass Transfer, 2016, 102:501-517. http://www.sciencedirect.com/science/article/pii/S0263822316313174
|
| [6] |
VILLIÈRE M, LECOINTE D, SOBOTKA V.Experimental determination and modeling of thermal conductivity tensor of carbon/epoxy composite[J].Composites Part A:Applied Science & Manufacturing, 2012, 504-506(46):60-68. http://www.sciencedirect.com/science/article/pii/S1359835X12003296
|
| [7] |
ZHANG X, FUJIWARA S, FUJⅡ M.Measurements of thermal conductivity and electrical conductivity of a single carbon fiber[J].International Journal of Thermophysics, 2000, 21(4):965-980. doi: 10.1023/A:1006674510648
|
| [8] |
XIE S, LI W, PAN Z, et al.Mechanical and physical properties on carbon nanotube[J].Journal of Physics & Chemistry of Solids, 2000, 61(7):1153-1158. http://www.sciencedirect.com/science/article/pii/S0022369799003765
|
| [9] |
YI W, LU L, ZHANG D L, et al.Linear specific heat of carbon nanotubes[J].Physical Review B Condensed Matter, 1999, 59(14):R9015. doi: 10.1103/PhysRevB.59.R9015
|
| [10] |
ZHANG X, XIE H, FUJⅡ M, et al.Thermal and electrical conductivity of a suspended platinum nanofilm[J].Applied Physics Letters, 2005, 86(17):171912-1-171912-3. doi: 10.1063/1.1921350
|
| [11] |
胡玉东, 刘锦辉, 王海东, 等.拉曼方法同时测量单根碳纤维热物性和对流传热系数[J].化工学报, 2014, 65(S1):251-257. http://www.cnki.com.cn/Article/CJFDTOTAL-HGSZ2014S1041.htm
HU Y D, LIU J H, WANG H D, et al.Simutaneous measurement of thermal properties and convective heat transfer coefficeient of individual carbon fiber using Raman spectroscopy[J].CIESC Journal, 2014, 65(S1):251-257(in Chinese). http://www.cnki.com.cn/Article/CJFDTOTAL-HGSZ2014S1041.htm
|
| [12] |
WANG H D, LIU J H, ZHANG X, et al.Raman measurements of optical absorption and heat transfer coefficients of a single carbon fiber in atmosphere environment[J].International Journal of Heat & Mass Transfer, 2014, 70(2):40-45. http://www.sciencedirect.com/science/article/pii/S0017931013009149
|
| [13] |
何凤梅, 李仲平, 冯志海, 等.PAN碳纤维高温热传输性能表征[J].中国材料进展, 2013, 32(4):236-241. http://www.cnki.com.cn/Article/CJFDTOTAL-XJKB201304010.htm
HE F M, LI Z P, FENG Z H, et al.Evaluation of thermal-transmission properties of PAN carbon fiber at hightemperature[J].Materials China, 2013, 32(4):236-241(in Chinese). http://www.cnki.com.cn/Article/CJFDTOTAL-XJKB201304010.htm
|
| [14] |
ALWAY-COOPER R M, THEODORE M, ANDERSON D P, et al.Transient heat flow in unidirectional fiber-polymer composites during laser flash analysis:Experimental measurements and finite element modeling[J].Journal of Composite Materials, 2012, 47(19):2399-2411. doi: 10.1177/0021998312458130
|
| [15] |
中华人民共和国国家质量监督检验检疫总局, 中国国家标准化管理委员会. 闪光法测量热扩散系数或导热系数: GB/T 22588-2008[S]. 北京: 中国标准出版社, 2009: 9-10.
General Administration of Quality Supervision, Inspection and Quarantine of the People's Republic of China, Standardization Administration of the People's Republic of China.Determination of thermal diffusivity or thermal conductivity by the flash method:GB/T 22588-2008[S].Beijing:Standards Press of China, 2009:9-10(in Chinese).
|
| [16] |
PILLING M W, YATES B, BLACK M A, et al.The thermal conductivity of carbon fibre-reinforced composites[J].Journal of Materials Science, 1979, 14(6):1326-1338. doi: 10.1007/BF00549304
|
Figures(7) / Tables(1)
Copyright © Journal of Beijing University of Aeronautics and Astronautics
Address: Editorial Department of Journal of Beijing University of Aeronautics and Astronautics, 37 Xueyuan Road, Haidian District, Beijing Post Code: 100191 Email: jbuaa@buaa.edu.cn
Supported by:
Beijing Renhe Information Technology Co., Ltd.
DownLoad: