Preparation of Al-Co codeposition coating on surface of Ni-based alloy

Faculty of Mechanical and Electronic Engineering, China University of Petroleum-Beijing, Beijing 102249, China

摘要

摘要: 利用包埋渗法在镍基高温合金表面成功制备了Al-Co涂层.涂层为单层结构,显示出均匀、致密的特性,涂层主要由AlNi相、AlCo相和Al-Cr间金属化合物组成.涂层中Al和Co的含量明显高于基体中两元素的含量.基体与涂层之间有一层与涂层厚度相当的过渡层,过渡层是由于其内部的Al元素向外扩散导致Cr,W,Mo,Ti等元素析出而形成的.过渡层与基体和涂层之间的结合都较为紧密,达到了冶金结合.
- 镍基合金 /
- 包埋渗 /
- 铝钴共渗 /
- 防护涂层 /
- 过渡层
Abstract: A novel Ni-Al-Co coating was developed through pack cementation for protection of superalloys. Surface and cross-sectional observations of the coated specimens were preformed on a scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS). X-ray diffraction (XRD) was used in order to detect the phases formed. The results show that the developed Ni-Al-Co coating, which is mainly composed of AlNi, AlCo and Al-Cr intermetallics, shows monolayer structure. The contents of Al and Co are obviously higher than that in the substrate. Furthermore, an interdiffusion layer has been developed between the Ni-Al-Co coating and the substrate. The interdiffusion layer shows good adherence on the substrate because no cracks and spalling was detected at the interface between the interdiffusion layer and the substrate. The formation of the interdiffusion layer may be induced by the precipitation of the elements of Cr,W,Mo,Ti during the pack cementation.
- Ni-based alloy /
- pack cementation /
- Al-Co codeposition /
- protective coating /
- interdiffusion layer

HTML全文

参考文献(1)

[1] 田晓东,郭喜平．铌基超高温合金表面Si-Al 包埋共渗抗氧化涂层的组织形成[J]．中国有色金属学报,2008,18(1):7-12 Tian Xiaodong,Guo Xiping．Structure formation of co-deposition of Si and Al coatings on advanced Nb-based ultrahigh temperature alloy by pack cementation process[J]． The Chinese Journal of Nonferrous Metals, 2008,18(1):7-12(in Chinese) [2] 王禹,郜嘉平,李云鹏,等．铌合金硅化物涂层的结构及高温抗氧化性[J]．无机材料学报,2000,15(1): 143-149 Wang Yu,Gao Jiaping,Li Yunping,et al.Microstructure and oxidation resistance of silicide coatings on niobium alloys[J].Journal of Inorganic Materials,2000,15(1): 143-149(in Chinese) [3] 赵陆翔,郭喜平,姜嫄嫄.铌基合金包埋渗法制备抗氧化硅化物涂层及其组织形成[J].中国有色金属学报,2007,17(4):596-601 Zhao Luxiang,Guo Xiping,Jiang Yuanyuan.Preparation and structural formation of oxidation-resistant silicide coatings on Nb-based alloy by pack cementation technique[J].The Chinese Journal of Nonferrous Metals,2007,17(4):596-601(in Chinese) [4] 刘培生．铝化物高温防护涂层的现状[J]．稀有金属材料与工程,2003,32(9):681-685 Liu Peisheng.Status of study on high-temperature oxidation law for aluminide coatings[J].Rare Metal Materials and Engineering,2003,32(9):681-685(in Chinese) [5] 李明,宋力昕,乐军,等.铌表面固体粉末包埋渗硅研究[J].无机材料学报,2005,3(20): 764-767 Li Ming,Song Lixin,Le jun,et al.Microstructure and mechanism of pack siliconizing on niobium[J]．Journal of Inorganic Materials,2005,3(20): 764-767(in Chinese) [6] 张鹏飞,李建平,蔡妍,等.K3 合金复合涂层高温防护性能研究[J].材料工程,2007,10:68-71 Zhang Pengfei,Li Jianping,Cai Yan,et al.Study of high temperature protective performance of composite coating on K3 superalloy[J]． Journal of Materials Engineering,2007,10:68-71(in Chinese) [7] Lu Tong,Yao Dengzun,Zhou Chungen.Low-temperature formation of aluminide coatings on Ni-base superalloys by pack cementation process[J].Chinese Journal of Aeronautics,2010,23(3):381-385 [8] 楼翰一．高温合金涂层与基体界面上的互扩散[J]．中国腐蚀与防护学报,1997,17(5):464-469 Lou Hanyi.Interdiffusion between high temperature coating and superalloy substrate [J].Journal of Chinese Society For Corrosion and Protection,1997,17(5):464-469(in Chinese) [9] 杨世伟．K4104合金Al-Si涂层抗高温氧化性能研究．哈尔滨:哈尔滨工程大学材料科学与化学工程学院,2006 Yang Shiwei.Research for high temperature oxidation properties of Al-Si coating on K4104 superalloy .Harbin:Colledge of Materials Science and Chemical Engineering,Harbin Institute of Technology,2006(in Chinese) [10] 李永作.K3合金Si-Al涂层的存在形式及分布[J]．金属学报,1984,20(2):94-102 Li Yongzuo.The existent form and distribution of Si-Al coating on K3 super alloy[J]． Journal of Metals,1984,20(2):94-102(in Chinese) [11] 赵陆翔．铌硅化物基超高温合金包埋渗Si层的组织形成及高温抗氧化性能．西安:西北工业大学材料学院,2007 Zhao Luxiang.Microstructural formation and high temperature oxidation resistance of pack siliconized coatings on an Nb silicide based alloy .Xi’an:School of Materials Science,Northwestern Polytechnical University, 2007(in Chinese) [12] Vialsi M,Francois M,Podor R．New silicides for new niobium protective coatings[J]．Journal of Alloys and Compounds,1998,264: 244-251 [13] Suzuki R O,Ishikawa M,Ono K．NbSi2 coating on niobiumusing molten salt[J]．Journal of Alloys and Compounds,2002,336: 280-284 [14] Xiang Z D,Datta P K.Pack aluminisation of low alloy steels at temperatures below 700℃[J].Surface and Coatings Technology,2004,184(1):108-115 [15] Xiang Z D,Rose S R,Datta P K.Low-temperature formation and oxidation resistance of nickel aluminide/nickel hybrid coatings on alloy steels[J].Scripta Materialia,2008,29(1): 99-102 [16] Zhao J C, Westbrook J H．Ultrahigh-temperature materials for jetengines[J]．MRS Bulletin,2003,9:622-630 [17] Zhan Zhaolin,He Yedong,Wang Deren,et al.Preparation of aluminide coatings at relatively low temperatures[J].Transactions of Nonferrous Metals Society of China,2006,16(3):647-653 [18] Kuo D H,Huang K W.A new class of Ti-Si-C-N coatings obtained by chemical vapor deposition-part II:Low-temperature process[J].Thin Solid Films,2001,394(1-2):80-88 [19] Xiang Z D,Datta P K,Codeposition of Al and Si on nickel base superalloys by pack cementation process[J].Materials Science and Engineering A,2003,356:136-144