Three-dimensional finite element analysis for non-synchronized cure of thick composite laminates

School of Aeronautic Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100191, China

摘要

摘要: 建立了描述厚截面复合材料固化压实过程的三维有限元模型并进行了模型有效性验证，计算了400层AS4/3501-6层合板在固化过程中的温度场、固化度、粘性、树脂体积含量和厚度压缩率情况.模型计算结果表明：在固化过程中，层合板的中间层会出现高于保温平台约49K的温度峰值；层合板沿厚度方向的温度和固化度的非同步现象明显；层合板的中部存在明显的局部温度过热和快速固化区域，该区域内的树脂粘性变化剧烈、树脂流动时间缩短，阻碍了该区域及层合板下部的多余树脂流入吸胶膜，并最终导致了固化结束后树脂的不均匀分布，靠近吸胶膜的上表面树脂体积含量约为41%，靠近模具的下表面约为46.5%；层合板的最终固化压实率在15.7%左右.
- 复合材料 /
- 厚截面 /
- 温度 /
- 固化度 /
- 粘性 /
- 树脂流动 /
- 有限元模型
Abstract: A three-dimensional finite element model was established and verified for the description of curing process of thick composite laminates. Temperature, degree of cure, viscosity, resin volume fraction and thickness reduction ratio during the curing process were calculated for a 400-ply AS4/3501-6 laminate. Numerical results manifest that the peak temperature which is 49K higher than the dwell temperature appears at the laminate's central ply; the changes of the temperature and degree of cure are not synchronized along the z-direction; the overshoot and quick-curing area is found evidently in the central part of the laminate; the viscosity varies greatly and the curing time is curtailed in this area, which prevent the spare resin in this area and under-part of the laminate flowing into the bleeder; the fact that the non-average distribution of the resin volume in the laminate stems from the existing of this area in the cure cycle, and the resin volume fraction is about 41% in the surface and 46.5% in the bottom which contact with the bleeder and the tool respectively; the approximate value of thickness reduction ratio is 15.7%.
- composites /
- thick section /
- temperature /
- degree of cure /
- viscosity /
- resin flow /
- finite element model

HTML全文

参考文献(14)

[1]	Twardowski T E, Geil P H.Curing in thick composite laminates:experiment and simulation[J].Journal of Composite Materials, 1993, 27 (3):216-250
[2]	Costa V A F, Sousa A C M.Modeling of flow and thermo-kinetics during the cure of thick laminated composites[J].International Journal of Thermal Sciences, 2003, 42 (1):15-22
[3]	Young W B.Compacting pressure and cure cycle for processing of thick composite laminates[J].Composites Science and Technology, 1995, 54:299-306
[4]	Young W B.Consolidation and cure simulation for laminated composites[J].Polymer Composites, 1996, 17 (1):142-148
[5]	Shin D D, Hahn H T.Compaction of thick composites:simulation and experiment[J].Polymer Composites, 2004, 25 (1):49-59
[6]	Kim J W, Lee J H, Kim H G, et al.Reduction of residual stresses in thick-walled composite cylinders by smart cure cycle with cooling and reheating[J].Composite Structures, 2006, 75 (1-4):261-266
[7]	Ganapathi A S, Joshi S C, Chen Z.Simulation of bleeder flow and curing of thick composites with pressure and temperature dependent properties[J].Simulation Modelling Practice and Theory, 2013, 32 (1):64-82
[8]	Guo Z S, Du S Y, Zhang B M. Temperature field of thick thermoset composite laminates during cure process[J].Composites Science and Technology, 2005, 65 (3/4):517-523
[9]	戴棣, 乔新.复合材料层合板的非同步固化翘曲变形分析[J].南京航空航天大学学报, 2000, 32 (1):63-68 Dai Di, Qiao Xin.Analysis of warpage deformation of composite laminates caused by non-synchronous curing[J].Journal of Nanjing University of Aeronautics & Astronautics, 2000, 32 (1):63-68 (in Chinese)
[10]	张纪奎, 关志东, 郦正能.热固性复合材料固化过程中温度场的三维有限元分析[J].复合材料学报, 2006, 23 (2):175-179 Zhang Jikui, Guan Zhidong, Li Zhengneng, Three-dimensional finite element analysis for the temperature field of thermoset composites during cure process[J].Acta Materiae Compositae Sinica, 2006, 23 (2):175-179 (in Chinese)
[11]	张纪奎, 郦正能, 关志东, 等.复合材料层合板固化压实过程有限元数值模拟及影响因素分析[J].复合材料学报, 2007, 24 (2):125-130 Zhang Jikui, Li Zhengneng, Guan Zhidong, et al.Compaction of laminated composites:numerical simulation and analysis on influencing factors[J].Acta Materiae Compositae Sinica, 2007, 24 (2):125-130 (in Chinese)
[12]	Gutowski T G.A resin flow/fiber deformation model for composites[J].SAMPE Quarterly, 1985, 16 (4):58-64
[13]	Hubert P.Aspects of flow and compaction of laminated composite shapes during cure[D].Province of British Columbia:The University of British Columbia, 1996
[14]	Ciriscioli P R, Wang Q L, Springer G S.Autoclave curing-comparisons of model and test results[J].Composite Materials, 1992, 26:90-102