Corrosion resistance characteristic of continuous basalt fiber and its reinforcing composites
-
摘要: 通过考察玄武岩纤维在蒸馏水、氢氧化钠溶液及盐酸中煮沸3h后的强度与质量变化,及其复合材料在8种化学介质中分别浸泡15d、30d和90d后的力学性能与表面形态变化,对一种国产连续玄武岩纤维及其复合材料的耐化学介质腐蚀性能进行了实验研究.结果表明,该玄武岩纤维及其复合材料都有很好的耐水及耐碱性能,且纤维的耐碱性能优于其耐酸性能.由于玄武岩纤维的耐酸碱性能差异,使复合材料具有如下腐蚀特性:酸性介质中,复合材料弯曲强度和弯曲模量同步降低;碱性介质中,复合材料弯曲强度降低,而弯曲模量几乎保持不变.Abstract: To explore the corrosion property of a new kind basalt fiber and its reinforcing composites, the basalt fiber was boiled 3h in water, sodium hydroxide and hydrochloric acid. The residual tensile strength and mass loss of basalt fiber after boiled were investigated. It was showed that the alkali resistance of the basalt fiber is better than acid resistance. To investigate the chemical durability of basalt composite in different mediums, samples were immersed in eight kinds of chemical mediums for 15, 30 and 90 days. After each period of immersion, the bending properties were tested and surface morphologies were observed. Study results reveal that the corrosion behavior of composite is very different in acid and alkaline due to the basalt fiber resistance difference. In acid mediums, the bending strength and bending module change in the same way. In alkaline mediums, bending module is very blunt compared with bending strength, bending module keeps close to the originality while bending strength declines gradually.
-
Key words:
- composites /
- basalt fiber /
- corrosion resistance /
- mechanical property
-
[1] 石钱华. 国外连续玄武岩纤维的发展及其应用[J]. 玻璃纤维,2003(4):27-31 Shi Qianhua. Overseas development and application of basalt continuous fiber[J]. Fiber Glass, 2003(4):27-31(in Chinese) [2] Sim J, Park C, Moon D Y. Characteristics of basalt fiber as a strengthening material for concrete structures[J]. Composites Part B Engineering,2005,36:504-512 [3] 王岚,陈阳,李振伟. 连续玄武岩纤维及其复合材料的研究[J]. 玻璃钢/复合材料, 2000(6):22-24 Wang Lan, Chen Yang, Li Zhenwei. Property of continuous basalt fiber and composites [J]. Fiber Reinforced Plastics/Composites, 2000(6):22-24(in Chinese) [4] 胡显奇,罗益锋,申屠年. 玄武岩连续纤维及其复合材料[J]. 高科技纤维及应用, 2002, 27(2):1-6 Hu Xianqi, Luo Yifeng, Shen Tunian. Basalt continuous fiber and its reinforcing composite material[J]. Hi-Tech Fiber & Application, 2002, 27(2):1-6(in Chinese) [5] 黄根来,孙志杰,王明超,等. 玄武岩纤维及其复合材料基本力学性能实验研究[J]. 玻璃钢/复合材料,2006(1):24-27 Huang Genlai, Sun Zhijie, Wang Mingchao, et al. Experimental research on mechanical properties of basalt fiber and composites[J]. Fiber Reinforced Plastics/Co-mposites, 2006(1): 24-27(in Chinese) [6] Militky J, Kovacic V, Rubnerová J. Influence of thermal treatment on tensile failure of basalt fibers[J]. Engineering Fracture Mechanics, 2002, 69:1025-1033
点击查看大图
计量
- 文章访问数: 3853
- HTML全文浏览量: 134
- PDF下载量: 868
- 被引次数: 0