Effects of Si on high temperature oxidation resistance of TiAl alloy

School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China

摘要

摘要: 利用X射线衍射、扫描电镜、能谱仪等手段研究了TiAl-Si(原子数分数为0~20%)合金在1 173 K大气中24 h的恒温氧化.结果表明:Si元素可以有效地提高TiAl合金的高温抗氧化性能;随着Si含量的增加,氧化膜厚度依次减薄,TiO₂的含量逐渐减少,Al₂O3的含量逐渐增加,添加到10%左右时就有连续致密的Al₂O₃保护膜形成;Si在0~20%的添加过程中并没发现Si的氧化物生成.分析表明:Si对抗氧化性能的贡献可归结于Si与Ti有很好的亲和力,可以有效地降低Ti离子的活度、阻碍Ti离子的向外扩散, 相对来说增强了Al离子的活度,促进连续致密的Al₂O₃保护膜生成.
- Si合金化 /
- TiAl合金 /
- 抗氧化性
Abstract: The isothermal oxidation of TiAl-Si(atom percent is 0~20%) alloys at 1 173 K, 24 hours on atmosphere were studied by X-ray diffraction,scanning electron microscopy and energy dispersive spectrum. The results reveals that the addition of Si improves the oxidation resistance of TiAl alloys. With increasing of Si content, the thickness of oxidation films and TiO₂ content are decreasing, and the content of Al₂O₃ is increasing. when the addition of Si reaches 10%, the continuous and compacted oxide film of Al₂O₃ is preferentially formed on the surface of TiAl alloy. During the addition of Si content from 0 to 20%, no any form of oxide of Si appears. The main reason of the improvement of oxidation resistance is attribute to Si combination with Ti, which results in the decrease of the activity of Ti, baffles Ti-ions outward diffusion, therefore relatively enhances the activity of Al, and the compacted oxide film of Al₂O₃ is preferentially formed on the surface of TiAl alloy.
- alloying with Si /
- TiAl alloy /
- oxidation resistance

HTML全文

参考文献(1)

[1] Kim Y W. Intermetallic alloys based on gamma titanium aluminide[J]. JOM, 1989, 41(42):24~30 [2] 周春根,徐惠彬,宫声凯,等.TiAl合金高温循环氧化行为及表面改性研究 . 航空学报,2000,21(1):87~89 Zhou Chungen, Xu Huibin, Gong Shengkai, et al. Cyclic oxidation behavior of TiAl and surface modification[J]. Acta Aeronautica et Astronautica Sinica, 2000,21(1):87~89(in Chinese) [3] Yamaguchi M. High-temperature structural intermetallics[J]. Acta Mater, 2000,48:307~405 [4] Jiang H, Hirohasi M, Imanari H, et al. The relationship between the morphology of the scale and the oxidation kinetics at elevated temperatures in Ti-Al alloys[J]. Scripta Materialia, 2001, 45:253~259 [5] Mckee D W, Huang S C. Oxidation behavior of gamma-titanium aluminide alloys under thermal cycling conditions[J]. Corros Sci, 1993,33:1899~1905 [6] 丁晓非,沈勇,王秀敏,等.W,Cr对高铌γ-TiAl基合金高温抗氧化性能的影响[J]. 稀有金属材料与工程,2004, 33(5):543~547 Ding Xiaofei, Shen Yong, Wang Xiumin, et al. Influence of W,Cr on the high-temperature oxidation resistance of γ-TiAl based alloys with high Nb content . Rear Metal Materials and Engineering, 2004, 33(5):543~547(in Chinese) [7] Varma S K, Chan A, Mahapatra R N. Static and cyclic oxidation of Ti-44Al and Ti–44Al–xNb alloys[J]. Oxid Met,2001,55:423~435 [8] Shimizu T, Likubo T, Isobe S. Cyclic oxidation resistance of an intermetallic compound TiAl[J] Mater Eng, 1992, A153:602~607 [9] Yoshihara M, Miura K. Effects of Nb addition on oxidation behavior of TiAl[J]. Intermetallics, 1995, 3:357~363 [10] 董利民,崔玉友,杨锐,等.元素Si对TiAl合金抗氧化性能的影响[J].金属学报,2004,40:383~387 Dong Limin, Cui Yuyou, Yang Rui, et al. Effects of element Si on oxidation resistance of TiAl alloys[J]. Acta Metallurgica Sonia, 2004,40:383~387(in Chinese) [11] 邱国华.金属间化合物Ti3Al/Ti5Si3合金研究 .上海:上海交通大学材料科学与工程学院,1993 Qiu Guohua. Research of intermetallic of Ti3Al/Ti5Si3 alloys . Shanghai:School of Materials Science and Engineering,Shanghai Jiaotong University, 1993 (in Chinese) [12] Jiang Huiren, Hirohasi M, Lu Yun, et al. Effect of Nb on the high temperature oxidation of Ti-(0-50at.%)Al[J]. Scripta Materialia, 2002,46:639~643