Research of accelerated corrosion test method of zinc, cadmium plating on high-strength steel

School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China

摘要

摘要: 采用加速盐雾、正交设计浸渍和合成海水浸渍3种加速腐蚀试验方法,考察了高强度钢锌、镉镀层实验室加速腐蚀与厦门外场大气腐蚀的相关性,由加速盐雾试验得到了适合于锌镀层的相关系数为0.995 2(显著相关)的线性回归方程.结果表明,加速盐雾试验对于锌、镉镀层的腐蚀均有明显的加速作用,正交设计浸渍试验中不含S^2-的溶液对镉镀层的腐蚀有明显的加速作用,合成海水浸渍试验对镉镀层的腐蚀有明显的加速作用.
- 高强度钢 /
- 加速试验 /
- 防护作用 /
- 镀层
Abstract: Using three accelerated corrosion tests in the lab, the relativity of accelerated corrosion in the lab and Xiamen marine atmosphere corrosion was studied to the zinc and cadmium plating coatings on the high-strength steel. The three methods selected are the accelerated salt spray test, orthogonal dipping test and resultant seawater dipping test. A linear regression equation is obtained with a correlative coefficient equal to 0.995 2(remarkably correlative) for the zinc plating. The results show that, the accelerating effect is remarkable for the zinc and cadmium plating coatings in the accelerated salt spray test as well as for the cadmium plating in the orthogonal dipping test of the solution without S^2-. And the accelerating action of the resultant seawater dipping test is effective to the cadmium plating.
- high-strength steel /
- accelerated testing /
- protective action /
- plating

HTML全文

参考文献(1)

[1] 屈庆,严川伟,张蕾.Zn初期大气腐蚀中NaCl和SO₂的协同效应[J].中国有色金属学报,2002,12(6):1272~1276 Qu Qing, Yan Chuanwei, Zhang Lei. The cooperated effect of NaCl and SO₂ for zinc initial corrosion in the atmosphere[J]. Journal of Chinese Colored Metal, 2002, 12(6):1272~1276( in Chinese) [2] Henriksen J F, Mikhailov A A. Atmospheric corrosion tests of metals in SO₂-polluted cold atmosphere in northern norway and along its border with Russia[J]. Protection of Metals, 2002, 38(6):579~589 [3] Panchenko Y M, Strekalov P V. Comparative assessment of zinc and cadmium electroplates by the weight of retained corrosion products and the total weight[J]. Protection of Metals, 2001, 37(4):367~384 [4] 李家柱,马颐军.锌镀层与镉镀层抗大气腐蚀性能的比较[J].材料工程,1998,(5):28~30,33 Li Jiazhu, Ma Yijun. The comparison of anti-corrosion ability in the atmosphere for zinc and cadmium plating[J]. Materials Engineering, 1998,(5):28~30, 33(in Chinese) [5] Zhirnov A D, Karimova S A, Ovsyannikova L V, et al. New protective coatings for replacing cadmium coatings on steel parts[J]. Metal Science and Heat Treatment, 2003, 45(1/2):23~25 [6] 王振尧, 于国才, 韩薇. 我国若干典型大气环境中的锌腐蚀[J]. 腐蚀科学与防护技术,2003,15(4):191~195 Wang Zhenyao, Yu Guocai, Han Wei. The zinc corrosion in some typical atmosphere in China[J]. Corrosion Science and Protection Technique, 2003, 15(4):191~195(in Chinese) [7] Gino Palumbo. The importance of subtle materials and chemical considerations in the development of accelerated tests for service performance prediction[S]. ASTM STP 1194, 1994.252~267 [8] 孙志华,李金桂,李牧铮.金属材料大气腐蚀加速试验研究的发展趋势[J].材料工程,1995,(12):41~43 Sun Zhihua, Li Jingui, Li Muzheng. The development trend of accelerated corrosion test studying for metal corrosion in atmosphere[J]. Materials Engineering, 1995,(12):41~43(in Chinese) [9] 刘慧丛,朱立群,杜岩滨.几种镀层海洋大气暴露与实验室盐雾试验条件下的耐腐蚀性研究[J].南昌航空工业学院学报(自然科学版),2002,(10):110~113 Liu Huicong, Zhu Liqun, Du Yanbin. The study of anti-corrosion ability of some plating coatings in marine atmosphere and salt spray corrosion test in the lab[J]. Journal of Nanchang Aerial Industrial Institute(Natural Science Edition), 2002,(10):110~113(in Chinese) [10] GB/T 10125—1997,人造气氛腐蚀试验——盐雾试验[S]B/T 10125—1997, Artificial ambience corrosion test——salt spray test[S]in Chinese) [11] HB/Z 5068—92,电镀锌、镉工艺[S]B/Z 5068—92, The technics of electroplating zinc, cadmium[S](in Chinese) [12] 章葆澄. 电镀工艺学[M]. 北京:北京航空航天大学出版社,1993.57,77 Zhang Baocheng. Electroplating technics[M]. Beijing:Beijng University of Aeronautics and Astronautics Press, 1993.57,77(in Chinese)