盐雾腐蚀对NiCoCrAlY涂层性能的影响

项民; 张琦; 骆军华

盐雾腐蚀对NiCoCrAlY涂层性能的影响

北京航空航天大学材料科学与工程学院北京 100083

基金项目: 航空基础科学基金资助项目(01151006)

详细信息

中图分类号: TG 1743
计量
- 文章访问数: 2975
- HTML全文浏览量: 142
- PDF下载量: 5
- 被引次数: 0
出版历程
- 收稿日期: 2004-04-28
- 网络出版日期: 2004-10-31

Influence of salt spray corrosion on the performance of NiCoCrAlY coatings

School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China

摘要

摘要: 利用中性盐雾试验对物理气相沉积制备的NiCoCrAlY防护涂层进行常温腐蚀,研究了常温盐雾腐蚀对NiCoCrAlY涂层的微观形貌以及高温性能的影响.试验结果表明:经过盐雾腐蚀的涂层表面的均匀性和完整性均被破坏,涂层表面产生了大量的腐蚀坑;高温循环氧化以后,表面形成的Al₂O₃氧化膜变得粗糙、破碎且不连续,而且氧化膜容易剥落,降低了涂层的高温抗氧化能力,缩短了涂层的使用寿命.
- 盐雾腐蚀 /
- 高温氧化试验 /
- NiCoCrAlY涂层
Abstract: The NiCoCrAlY coatings prepared by electron beam physical vapor deposition (EB-PVD) was studied by a salt-spray-test. The influence of salt spray corrosion on the microstructure and high-temperature cyclic oxidation behavior of NiCoCrAlY coating was investigated. Results show that the alumina formed on the corroded NiCoCrAlY coating is roughness, cracked and incontinuous and many pits was formed on the surface of the coating after the salt-spray test. The Al₂O₃ films formed within the pit are rougher, which suggests the congregation of stresses and spallation of the oxide film during the cyclic oxidation. These changes will reduce the protection ability of the coatings during high-temperature oxidation and shorten the lifetime of cyclic oxidation of NiCoCrAlY coatings.
- salt air corrosion /
- high-temperature oxidation tests /
- NiCoCrAlY coating

HTML全文

参考文献(1)

[1] Goward G W. Progress in coatings for gas turbine airfoils[J]. Surface & Coatings Technology, 1998, 108-109:73~79 [2]Padture N P, Gell M, Jordan E H. Thermal barrier coatings for gas-turbine engine application[J]. Science, 2002,296:280~284 [3] 王冰,宫骏,黄美东,等.合金元素在MCrAlY涂层中的行为[J].材料保护,2001,34(4):1~3 Wang Bing, Gong Jun, Huang Meidong, et al. Behavior of element in MCrAlY coating[J]. Materials Protection, 2001,34(4):1~3(in Chinese) [4] 杨永强.钇在McrAlY激光熔覆层中的存在形式及作用[J].华南理工大学学报,1998,26(9):65~68 Yang Yongqiang. Existent forms and effects of yttriumin laser claddings of MCrAlY[J]. Journal of South China University of Technology,1998,26(9):65~68(in Chinese) [5] 李美女亘 ,孙晓峰,张重远,等. 溅射NiCrAlY涂层氧化过程Al₂O₃膜结构与形貌的转变[J].腐蚀科学与防护技术,2002,14(3):142~146 Li Meimeng, Sun Xiaofen,Zhang Zhongyuan, et al. Phase and morphology transformation of Al₂O₃ during oxidation of sputtered NiCrAlY coatings[J]. Corrosion Science and Protection Technology, 2002,14(3):142~146(in Chinese)