Interdiffusion behavior in Nb/α-Ti3Al ternary system
-
摘要: 采用反应扩散偶的方法,研究了Nb元素在α-Ti3Al中的扩散行为.反应扩散偶经过120 h扩散退火,在高温(1 573 K)下生成了均匀的β-(Ti,Nb)扩散层;低温(1 273,1 423 K)下生成不均匀的扩散区,相组成为Ti3Al(Nb),β-(Ti,Nb)及Nb2Al.采用Dayananda方法计算了体系的扩散系数,即根据一个扩散偶的浓度分布曲线计算体系的扩散系数.采用平均扩散系数来表征体系的扩散系数,得出扩散模型和相关扩散机理.结果表明:Ti和Al的主扩散系数比Nb的主扩散系数大5个数量级;Ti的主扩散系数约是Al的2倍.Nb通过占据Ti的空位进行扩散,Nb的掺入阻碍了Ti元素扩散,从而提高了α-Ti3Al体系的高温抗氧化性能.
-
关键词:
- 氧化 /
- 扩散 /
- 互扩散 /
- Nb/α-Ti3Al
Abstract: The α2 single phase interdiffusion behavior in Ti3Al-Nb ternary system was studied at the temperature of 1 273 K, 1 423 K, 1 573 K, using Ti3Al/Nb single phase diffusion couples. The uniform β-(Ti, Nb) phase was formed in mid of the diffusion couple after 120 hours diffusion annealing in the high temperature. On the contrary, the nonuniform diffusion layers, including Ti3Al(Nb), β-(Ti,Nb) and Nb2Al, were formed in low temperature.The interdiffusion coefficients were calculated by the method of Dayananda, which can evaluate by the concentration dependence in one couple only. The calculation results show that the interdiffusion coefficients of Ti and Al is five order of magnitude larger than Nb, and Nb atoms are considered to occupy Ti sites in Ti3Al, the exchanges with vacancies on Ti sublattice played a leading role in the diffusion of Ti3Al. These results can provide a theoretical basis for the mechanisms of Nb improving the oxidation resistance of Ti3Al.-
Key words:
- oxidation /
- diffusion /
- interdiffusion /
- Ti3Al-Nb
-
[1] Kim Y W.Microstructural evolution and mechanical properties of a forged gamma titanium aluminide alloy[J].Acta Metallurgica et Materialia,1992,40(6):1121-1134 [2] Liu C T.Recent advances in ordered intermetallics[J].Materials Chemistry and Physics,1995,42(2):77-86 [3] Yamaguchi M,Inui H,Ito K.High-temperature structural intermetallics[J].Acta Materialia,2000,48(1):307-322 [4] Chu M S,Wu S K.Improvement in the oxidation resistance of α2-Ti3A1 by sputtering Al film and subsequent interdiffusion treatment[J].Surface Coating Technology,2004,179(2/3):257-264 [5] Fang Wei,Ko Se Hyun,Hashimoto Hitoshi.High temperature oxidation behavior of Ti3Al-Nb alloys prepared by pulse discharge sintering[J].Material Science and Engineering:A,2002,329/330/331:708-713 [6] Wang Yanhang,Lin Junpin,He Yuehui,et al.Reaction mechanism in high Nb containing TiAl alloy by elemental powder metallurgy[J].Transactions of Nonferrous Metals Society of China,2006,16(4):853-857 [7] 王兴军,常海威,雷明凯.Nb合金化γ-TiAl的氧化热力学理论分析[J].金属学报,2001,37(8):811-814 Wang Xingjun,Chang Haiwei,Lei Mingkai.Thermodynamic aspects of oxidation for Nb alloying γ-TiAl intermatallic compounds[J].Acta Matallurgica Sinica,2001,37(8):811-814(in Chinese) [8] Rüsing J,Herzig C.Concentration and temperature dependence of titanium self-diffusion and interdiffusion in the intermetallic phase Ti3Al[J].Intermetallics,1996,4(8):647-657 [9] Brever J,Wilger T,Friesel M,et al.Interstitial and substitutional diffusion of metallic solutes in Ti3Al[J].Intermetallic,1999,7(3/4):381-388 [10] Dayananda M A.Average effective interdiffusion coefficients and matano plane composition[J].Metallurgical and Materials Transactions A,1996,27(9):2504-2509 [11] Dayananda M A.A new analysis for the determination of ternary interdiffusion coefficients from a single diffusion couple[J].Metallurgical and Materials Transactions A,1999,30(3):535-543 [12] Tororic P C,Dayananda M A.Interdiffusion and diffusion structure development in selected refractory metal silicides[J].Materials Science and Engineering:A,1999,261(1/2):64-77 [13] Cermak J,Rothova V.Concentration dependence of ternary interdiffusion coefficients in Ni3Al/Ni3Al-X couples with X=Cr,Fe,Nb and Ti[J].Acta Materialia,2003,51(15):4411-4421 [14] Garimella N,Ode M,Ikeda M.Effects of Ir or Ta alloying addition on interdiffusion of L12-Ni3Al[J].Intermetallics,2008,16(9):1095-1103 [15] Yao Dengzun,Yang Junying,Gong Weiyan,et al.Interdiffusion behavior between Nb and MoSi2 intermetallic compound[J].Materials Science and Engineering:A,2010,527(26):6787-6793 [16] Wei Haixia,Gong Weiyang,Huang Sheng,et al.Single-phase interdiffusion in the Ni3Al-Mo ternary system[J].Scripta Materialia,2011,64(1):53-56 -
点击查看大图
计量
- 文章访问数: 1874
- HTML全文浏览量: 219
- PDF下载量: 538
- 被引次数: 0
下载: