电镀法制备超疏水性铜表面

乔贞美; 席文君; 朱春雷; 贾 傲

电镀法制备超疏水性铜表面

北京航空航天大学材料科学与工程学院, 北京 100191

详细信息

作者简介:
乔贞美(1981-),女,山东泰安人,硕士生,xiwj@buaa.edu.cn.

中图分类号: TQ 153.1⁺4
计量
- 文章访问数: 3202
- HTML全文浏览量: 30
- PDF下载量: 1833
- 被引次数: 0
出版历程
- 收稿日期: 2007-10-16
- 网络出版日期: 2008-12-31

Preparation of superhydrophobic copper surfaces by electroplating

School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100191, China

摘要

摘要: 在对天然荷叶表面观察的基础上,通过改变电流密度控制电镀层表面的形貌,制备出了仿荷叶结构的铜表面.随着电镀电流密度的逐渐增大,接触角先增大后减小,当电流密度为0.08 A/cm²时,镀层的表面结构与荷叶表面最接近,其疏水效果最好,接触角最大,达到了153.5°,滚动角为7.9°(小于10°).这种表面未经任何修饰就产生了超疏水性.这是处于Cassie模型的一种亚稳定状态,只要表面形貌特征满足一定条件,就可使水滴在亲水基体上处于Cassie模型的亚稳态,从而有可能产生疏水性甚至超疏水性.对亲水材料的疏水机理进行了探讨,这些结果对亲水基体上超疏水性表面的制备和现有疏水理论的理解具有一定的意义.
- 超疏水性 /
- 电镀 /
- 荷叶结构
Abstract: The structure of the natural superhydrohlbic surface, lotus leaf, was studied, which inspired the fabrication method of superhydrophobic surfaces. Various copper surfaces were fabricated in different current densities via electroplating. As the current density increased, the water contact angle (CA) increased first and then decreased. When the current density was about 0.08 A/cm², the electroplated copper surface which resembled the lotus leaf reached superhydrophobic state (CA=153.5°, SA (sliding angle) = 7.9°). The surface with lotus leaf structure is superhydrophobic without any surface modification. It-s suggested that this is a meta-stable state in Cassie state. As long as the surface structure is suitable, a hydrophobic surface could be gotten, or even superhydrophobic surface, on hydrophilic materials. The hydrophobic mechanism was also analyzed. The results widen the horizon of fabricating superhydrophobic surfaces on hydrophilic materials and give light to the existing popular theories.
- superhydrophobic /
- electroplating /
- lotus leaves structure

HTML全文

参考文献(1)

[1] Blossey R. Self-cleaning surfaces-virtual realities[J]. Nature Materials,2003,2:301-306 [2] Lafuma A, Quere D. Superhydrophobic states[J]. Nature Materials,2003,2:457-460 [3] Feng L, Li S, Li Y, et al. Super-hydrophobic surfaces: from natural to artificial[J]. Adv Mater,2002,14:1857-1860 [4] Wenzel R N. Resistance of solid surfaces to wetting by water[J]. Ind Eng Chem,1936,28:988-994 [5] Cassie A, Baxter S. Wettability of porous surfaces[J].Trans Faraday Soc,1944,40:546-551 [6] Feng Xinjian, Jiang Lei. Design and creation of superwetting/antiwetting surfaces[J]. Adv Mater,2006,18:3063-3078 [7] Nishino T, Meguro M, Nakamae K, et al. The lowest surface free energy based on CF3 alignment[J]. Langmuir,1999,15:4321-4323 [8] Shirtcliffe N J,McHale G,Newton M I,et al. Wetting and wetting transition on copper-based super-hydrophobic surfaces[J]. Langmuir,2005,21(3):937-943 [9] Tsujii K, Yamamoto T, Onda T, et al. Super oil-repellent surfaces[J]. Angew Chem,1997,36(9):1011-1012 [10] Shibuichi S, Onda T, Tsujii K, et al. Super water-and oil-repellent surfaces resulting from fractal structure[J]. J Colloid Interface Sci,1998,208(1):287-294 [11] Sun T L,Zhu D B,Lin F,et al.Manipulation of surface wettability between superhydrophobicity and superhydrophilicity on copper films[J]. Chem Phys Chem,2005,6(8):1475-1478 [12] Shirtcliffe N J,McHale G,Newton M I,et al. Dual-scale roughness produces unusually water-repellent surfaces[J]. Adv Mater,2004,16(21):1929-1932 [13] Barthlott W, Neinhuis C. Purity of the sacred lotus, or escape from contamination in biological surfaces[J]. Planta,1997,202(1):1-8 [14] 覃奇贤,郭鹤桐,刘淑兰,等.电镀原理与工艺[M].天津:天津科学技术出版社,1993:40-41 Tan Qixian, Guo Hetong, Liu Shulan,et al. Principles and technics of electroplating[M]. Tianjin:Tianjin Publishing Company of Science and Technology,1993:40-41(in Chinese) [15] 胡汉起.金属凝固原理[M].北京:机械工业出版社,2000:130-131 Hu Hanqi. Theories of metal solidification [M]. Beijing:China Machine Press,2000:130-131(in Chinese) [16] Patankar N A. On the modeling of hydrophobic contact angles on rough surfaces[J].Langmuir,2003,19(4):1249-1253 [17] Marmur A. Wetting on hydrophobic rough surfaces: to be heterogeneous or not to be[J].Langmuir,2003,19(20):8343-8348