Fatigue life evaluation and test verification for civil aircraft structure under corrosive environment
-
摘要: 针对民机结构典型疲劳关键部位——机翼弦向对接部位,进行了腐蚀条件下民机结构疲劳寿命评定方法合理性的试验验证,评定了该部位腐蚀条件下疲劳寿命.通过关键部位细节模拟试件加速预腐蚀及随后的一般环境下疲劳试验,测定了预腐蚀影响系数曲线;通过腐蚀疲劳试验测定了腐蚀疲劳影响系数;通过关键部位大型结构模拟试件预腐蚀-腐蚀疲劳交替验证试验,测定了典型使用情况下的腐蚀综合修正系数,同时用腐蚀条件下民机结构疲劳寿命评定方法针对交替试验情况进行了评定,结果对比表明该评定方法是合理、可行的.并给出了机翼弦向对接部位典型使用情况下的疲劳寿命评定结论.Abstract: Rationality of the fatigue life evaluated method for civil aircraft structures under corrosive environment was validated by test for the chordwise joint parts of wings which were typical fatigue critical parts of civil aircraft structures. And the fatigue life of this part under corrosion was evaluated. The pre-corrosion curve was obtained by pre-corrosion and followed fatigue test in common environment on simulated specimens of this critical part. The corrosion-fatigue influence factor was obtained by corrosion-fatigue test on the same specimens. Pre-corrosion and corrosion-fatigue alternation tests were carried out on large-scale simulated specimens. And the synthetical correction factor of corrosion under typical using condition was obtained. The correction factor of the alternative test was also obtained by evaluated method. The comparison between the two results shows that the evaluated method is rational and validity. And the fatigue life evaluated result of the chordwise joint parts of wings under corrosion was given.
-
Key words:
- corrosion /
- corrosion fatigue /
- civil aircraft /
- fatigue life
-
[1] David L Simpson, Craig L Brooks. Tailoring the structural integrity process to meet the challenges of aging aircraft[J]. International Journal of Fatigue,1999,21:s1-s14 [2] Margery E Hoffman, Paul C Hoffman. Corrosion and fatigue research——structural issues and relevance to naval aviation[J]. International Journal of Fatigue,2001,23:s1-s10 [3] 郑晓玲, 李令芳. 民机结构耐久性与损伤容限设计手册(上册)——疲劳设计与分析[M]. 北京:航空工业出版社,2003 Zheng Xiaoling, Li Lingfang. Handbook of durability and damage tolerance design of civil aircraft structure (vol.1)——fatigue design and analysis[M]. Beijing:Aviation Industry Press, 2003(in Chinese) [4] 刘文珽, 李玉海, 贾国荣. 腐蚀条件下飞机结构使用寿命的评定与监控[J]. 北京航空航天大学学报,1996,22(3):259-263 Liu Wenting, Li Yuhai, Jia Guorong. Evaluation and supervision of service life for aircraft structures under corrosive condition[J]. Journal of Beijing University of Aeronautics and Astronautics, 1996, 22(3):259-263(in Chinese) [5] 李玉海. 腐蚀条件下飞机结构寿命体系评定技术研究 . 北京:北京航空航天大学航空科学与工程学院,2001 Li Yuhai. A research on evaluating technique for life system of aircraft structures under corrosive condition . Beijing:School of Aeronautic Science and Technology, Beijing University of Aeronautics and Astronautics, 2001(in Chinese) [6] 贺小帆. 腐蚀条件下飞机结构寿命可靠性关键技术研究 . 北京:北京航空航天大学航空科学与工程学院,2003 He Xiaofan. Research on life reliability key techniques for aircraft structures under corrosion condition . Beijing:School of Aeronautic Science and Technology, Beijing University of Aeronautics and Astronautics, 2003(in Chinese) [7] 刘文珽, 杨洪源, 贺小帆. 腐蚀条件下民机结构疲劳寿命评定方法研究[J]. 北京航空航天大学学报,2004,30(8):753-756 Liu Wenting, Yang Hongyuan, He Xiaofan. Evaluation of fatigue lives for civil aircraft structures under corrosive conditon[J]. Journal of Beijing University of Aeronautics and Astronautics, 2004, 30(8):753-756(in Chinese) -
点击查看大图
计量
- 文章访问数: 3748
- HTML全文浏览量: 222
- PDF下载量: 1093
- 被引次数: 0
下载: