Investigation of probability failure assessing curve of steel used as pressure vessel material produced in China

1.
School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China
2. School of Mechanical Science and Engineering, Changchun University of Technology, Changchun 130012, China

摘要

摘要: 随着概率安全评定技术(PSA,Probabilistic Safety Assessment)的发展,该技术已经开始逐步向工程应用领域渗透,但其在应用方面还存在若干的问题,失效评定曲线的概率化就是其主要问题之一.对多个厂家、多种炉号、多种板厚4种国产钢种5种裂纹形式的大量失效评定曲线进行了概率分析,采用三段分析法和逼近法得到了不同可靠度下的4种国产钢的概率失效评定曲线及其表达式,以及一般长屈服平台国产钢在不同可靠度下的一般失效评定曲线及其表达式.运用这些表达式可实现适合我国国产钢种含缺陷构件的工程概率安全评定分析.
- 概率安全评定 /
- 概率失效评定曲线 /
- 国产压力容器用钢
Abstract: Along with the development of the theory and the technology of PSA(probabilistic safety assessment),the theory and the technology has been used on the engineering field. But there are many problems that are not clear both in theory and technology of PSA. Probabilize of failure assessment curve is one of the significant problems among them. To solve this problem plenty of probabilistic analysis have been carried on the failure assessment curves of 5 kinds of crack styles of four kinds of steel produced in different Chinese steel makers, different heat and different thickness. Probabilistic assessment curve of four kinds of steel and general steel which has long yield point elongation that manufactured in China on different reliability have been obtained by the three-part analysis way and closing approach. The equations are valuable for the engineering probabilistic safety assessment of the long yield point elongation steel manufactured in China.
- probabilistic safety assessment /
- probability failure assessment curve /
- steel used as pressure vessel material produced in China

HTML全文

参考文献(1)

[1] 王明娥,戴树和. 高温高压换热器的可靠性分析——FTA方法的应用[J].压力容器,1986,3(1):23~31 Wang Minge,Dai Shuhe. Application of reliability analysis——FTA on high temperature high pressure heat exchanger[J]. Pressure Vessel, 1986,3(1):23~31(in Chinese) [2] Dai Shuhe. Life extension, reliability analysis and expert system for the assessment of fatigue damage in structure with welded defects——a study of applications of high technology in reliability analysis for pressure vessel technology[J]. Int J Pres Ves & Piping, 1993,56(3):263~273 [3] Bullough R, Green V R, Tomkins B,et al. Areview of methods and applications of reliability analysis for structural integrity assessment of UK nuclear plant[J]. International Journal of Pressure Vessels and Piping, 1999,76(13):909~919 [4] 武淮生,钟群鹏.飞机发动机零部件结构完整性的概率R6评定[J].航空学报,2000,21(4):96~99 Wu Huaisheng, Zhong Qunpeng. Probabilistic R6 assessment for structure integrity of aircraft engine componets[J].Acta Aeronautic et Astronautica Sinica,2000,21(4):96~99 [5] Jin X, Zhong Q P. A probalilistic fracture mechanics assessment method based on the R6 procedure[J]. Int J Pres Ves and Piping, 1997,73(2):161~163 [6] Wu H S, Zhong Q P. Assessment for integrity of structures containing defects[J]. Int J Pres Ves and Piping, 1998,75(4):343~346 [7] Giribone R, lValette B. Principles of failure probability assessment(PoF)[J]. International Journal of Pressure Vessels and Piping,2004,81(10-11):797~806 [8] 王志文.在役压力容器对接焊缝区面型缺陷弹塑性断裂分析及评定研究 .上海:上海理工大学,85-924-02-02,1995 Wang Zhiwen, Investigation of elastic-plastic fracture analysis and assessment for surface defects on butt welding district of in-service pressure vessles. . Shanghai:East China University of Science & Technology, 85-924-02-02, 1995 [9] 叶卫平, 方安平, 于本方.Origin 7.0科技绘图及数据分析[M]. 北京:机械工业出版社, 2004 Ye Weiping, Fang Anping, Yu Benfang. Origin 7.0 science & technology drawing and data analysis[M].Beijing:Mechanical Industry Press,2004