Effect of cyclic hygrothermal environment on interfacial property of CCF300/BMI composites

School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100191, China

摘要

摘要: 针对CCF300/5428复合材料在循环湿热环境下的吸湿-脱湿行为和层间剪切性能进行了研究,并结合扫描电镜观察了循环湿热处理的不同阶段纤维/基体界面结合状态.研究结果表明:经过反复吸湿后,水分的初始扩散速率和饱和吸湿率增加;脱湿后水对复合材料层间剪切性能的影响大部分可以消除;复合材料吸湿后室温环境下性能下降较少,但在高温高湿环境下,复合材料的性能会显著降低.
- 碳纤维 /
- 复合材料 /
- 湿热循环 /
- 层间剪切性能
Abstract: An experimental investigation was conducted in order to study the effect of cyclic hygrothermal environment on the interfacial property of CCF300/5428 composites. The moisture weight and interlaminar shear strength(ILSS) of CCF300/5428 specimens of each stage during three absorption-desorption cyclical processes were tested. The morphology of interface between carbon fiber and resin was characterised by applying scanning electron microscope(SEM) method. The results show that the composites exhibit higher diffusivity after suffering reabsorption steps. The reversible effects of water on ILSS of the composites can be eliminated after desorption. The ILSS of the composites degrade obviously due to high temperature, while the humidity has weak effect on the mechanical performance of the composites at room temperature.
- carbon fiber /
- composites /
- cyclic hygrothermal /
- interlaminar shear strength(ILSS)

HTML全文

参考文献(1)

[1] Kumar S B,Sridhar I,Sivashanker S.Influence of humid environment on the performance of high strength structural carbon fiber composites[J].Materials Science and Engineering A,2008,498(1):174-178 [2] Mercier J,Bunsell A,Castaing P ,et al.Characterisation and modelling of aging of composites[J].Composites A,2008,39 (2):428-438 [3] Wan Y Z,Wang Y L,Huang Y,et al.Hygrothermal aging behaviour of VARTMed three-dimensional braided carbon-epoxy composites under external stresses[J].Composites A,2005,36(8): 1102-1109 [4] Biro D A,Pleizer G,Deslandes Y.Application of the microbond technique:effects of hydrothermal exposure on carbon-fiber/epoxy interfaces[J].Composites Science and Technology,1993,46 (3):293-301 [5] Zhou J,Lucas J P.The effects of a water environment on anomalous absorption behavior in graphite/epoxy composites[J].Composites Science and Technology ,1995,53(1):57-64 [6] Imaz J J,Rodrigurz J L,Rubio A,et al.Hydrothemal environment influence on water diffusion and mechanical behaviour of carbon fibre/epoxy laminates[J].Materials Science Letters,1991,10(11):662-665 [7] Selzer R,Friedrich K.Mechanical properties and failure behaviour of carbon fibre-reinforced polymer composites under the influence of moisture[J].Composites A ,1997,28(6):595-604 [8] Wang C,Wang J,Su T,Determination of water diffusion coefficients and dynamics in adhesive/carbon fiber-reinforced phenolic resin composite joints[J].Adhesion ,2007,83(3): 255-265 [9] Favre J P,Interfacial phenomena in composite materials //Jones F R.Proceedings of the international conference.Sheffield UK:Butterworths,1989:7-12 [10] Apicella A,Nicolais L.Hygrothermal history dependence of equilibrium moisture sorption in epoxy resins[J].Polymer,1981,22(8):1064-1067 [11] 黄玉东,魏月贞.复合材料界面研究现状(下)[J].纤维复合材料,1994(2): 5-8 Huang Yudong,Wei Yuezhen.Current research status of composites interphase[J].Fiber Composites,1994(2):5-8(in Chinese) [12] Sarti G C,Apicella A.Non-equilibrium glassy properties and their relevance in case II transport kinetics[J].Polymer,1980,21(9):1031-1036 [13] 王恒武,王继辉 ,朱京杨.纤维增强树脂基复合材料界面粘结强度测试方法探讨[J].玻璃钢/复合材料,2003(3):42-45 Wang Hengwu,Wang Jihui,Zhu Jingyang.Discussion on measurement methods of interfacial adhesion strength of fiber reinforced polymer composites[J].FRP/CM,2003(3):42-45(in Chinese) [14] Choi N,Park J.Fiber/matrix interfacial shear strength measured by a quasi-disk microbond specimen[J].Composites Science and Technology,2009,69(10):1615-1622 [15] Maggana G,Pissis P.Water sorption and diffusion studies in an epoxy resin system[J].Polymer Science Part B: Polymer Physics ,1999,37(11):1170-1182 [16] 郑路,常新龙,赵峰.湿热环境中符合材料吸湿性研究[J].纤维复合材料,2007(2): 37-39 Zheng Lu,Chang Xinlong,Zhao Feng.Research on moisture absorption of composites in the hydrothermal environment[J].Fiber Composites,2007(2):37-39(in Chinese) [17] 李静.纤维增强树脂基复合材料的吸湿性和湿变形[J].航天返回与遥感,2010(2): 69-71 Li Jing.Moisture absorption and soaking deformation of fiber reinforced resin composites[J].Spacecraft Recovery ＆ Remote Sensing,2010(2):69-71(in Chinese) [18] 过梅丽,肇研.航空航天结构复合材料湿热老化机理的研究[J].宇航材料工艺,2002(4) :51-54 Guo Meili,Zhao Yan.Study on hyrothermal ageing mechanisms of aerospace structural composites[J].Aerospace Materials & Technology,2002(4):51-54(in Chinese) [19] Shen C H.Moisture absorption and sesorption of composite materials[J].Composite Materials,1976,10(1):2-20 [20] Apicella A,Nicolais L.Effect of thermal history on water sorption,elastic properties and the glass transition of epoxy resins [J].Polymer,1979,20(9):1143-1148 [21] Wong T C,Broutman L J.Moisture diffusion in epoxy resins part I:non-fickian sorption processes[J].Polymer Engineering Science,1985,25(9):521-528 [22] Connelly R W,McCoy N R,Hopfenberg H B,et al.The effect of sorbed penetrants on the aging of previously dilated glassy polymer powders I lower alcohol and water sorption in poly(methyl methacrylate) [J].Applied Polymer Science,1987,34(2):703-719 [23] Stewart M E,Hopfenberg H B,McCoy N R.The effect of sorbed penetrants on the aging of previously dilated glassy polymer powders II:n-propane sorption in polystyrene[J].Applied Polymer Science,1987,34(2):721-735 [24] Zainuddin S,Hosur M V,Zhou Y.Durability study of neat/nanophased GFRP composites subjected to different environmental conditioning[J].Materials Science and Engineering A ,2010,527(13/14):3091-3099 [25] Ray B C.Temperature effect during humid ageing on interfaces of glass and carbon fibers reinforced epoxy composites[J].Colloid and Interface Science,2006,298(1):111-117 [26] Akbar S,Zhang T.Moisture diffusion in carbon/epoxy composite and the effect of cyclic hygrothermal fluctuations: characterization by dynamic mechanical analysis (DMA) and interlaminar shear strength (ILSS)[J].Adhesion,2008,84(7):585-600