Thermal analysis for dynamic behavior of microcellular polycarbonate
-
摘要: 通过对聚碳酸酯微孔塑料进行动态力学热分析,得到了不同密度微孔塑料动态力学性能的温度图谱和频率图谱,研究了储能模量和损耗因子与温度、频率及密度之间的变化规律和玻璃化转变温度与密度之间的关系.结果表明:在高频或低温时,随着温度的升高,微孔塑料储能模量降低,损耗因子增加;当温度高于材料的玻璃化转变温度或者频率较低时,随着频率的降低和温度的升高,储能模量和损耗因子都急剧地降低;聚碳酸酯微孔塑料的玻璃化转变温度Tg在175°C左右,次级转变在70~100℃之间,结果与密度几乎无关.Abstract: The dynamic behavior of microcellular polycarbonate for different densities at different temperatures and frequencies was investigated by means of dynamic mechanical thermal analysis. The relations of storage modulus and loss factor with temperature, frequency and density were discussed at the same time.Furthermore, the relation of glass transition temperature of microcellular polycarbonate with density was also discussed. The results show that when the microcellular polycarbonate is at high frequency or low temperature, the storage modulus is decreased and the loss factor is increased with increasing temperature. Meanwhile, when the temperature is higher than the glass transition temperature of microcellular polycarbonate or the frequency is very low, the storage modulus and the loss factor are decreased significantly with increasing temperature or decreasing frequency . In addition, the experimental results also show that the glass transition temperature of microcellular polycarbonate is about 175℃ and the secondary transition temperature of microcellular polycarbonate is in the range of 70~100℃, which almost have nothing to do with density.
-
Key words:
- microcellular plastics /
- dynamic behavior /
- visco-elasticity /
- storage modulus /
- loss factor
-
[1] 卢子兴. 微孔泡沫塑料力学行为的研究综述[J].力学进展, 2002,32(3):365-378 Lu Zixing. A review of studies on the mechanical behavior of microcellular plastics[J]. Advances in Mechanics, 2002, 32(3):365-378(in Chinese) [2] Shimbo M, Baldwin D F, Suh N P. The viscoelastic behavior of microcellular plastics with varying cell size[J]. Polym Eng Sci,1995:35(17):1387-1393 [3] Jae D Y, Sung W C. Change of glass transition temperature of polymers containing gas[J]. Polymer Testing, 2001(20):287-293 [4] 过梅丽.高聚物与复合材料的动态力学热分析[M]. 北京:化学工业出版社,2002 Guo Meili. Thermal analysis for dynamic behavior of polymer and composites[M]. Beijing:Chemical Industry Press, 2002(in Chinese) [5] 卢子兴, 张慧. 聚碳酸酯微孔塑料的拉伸力学性能及本构关系[M]. 北京航空航天大学学报, 2004,30(3):202-205 Lu Zixing, Zhang Hui. Tensile mechanical properties and constitutive relation of microcellular polycarbonate[J]. Journal of Beijing University of Aeronautics and Astronautics, 2004,30(3):202-205(in Chinese) -
点击查看大图
计量
- 文章访问数: 2752
- HTML全文浏览量: 161
- PDF下载量: 1291
- 被引次数: 0
下载: